Article comprising poly(phenylene ether)-polysiloxane copolymer composition

ABSTRACT

Articles exhibiting flame retardancy and heat resistance are fabricated from a composition that includes specific amounts of a poly(phenylene ether)-polysiloxane block copolymer reaction product, a flame retardant, and a reinforcing filler. Articles benefitting from the composition&#39;s properties include fuser holders for electrophotographic copiers, fan blades, battery parts for hybrid and electric vehicles, parts for automotive kinetic energy recovery systems, and electric vehicle junction boxes.

BACKGROUND OF THE INVENTION

Poly(phenylene ether) is a type of plastic known for its excellent waterresistance, dimensional stability, and inherent flame retardancy.Properties such as strength, stiffness, chemical resistance, and heatresistance can be tailored by blending it with various other plastics inorder to meet the requirements of a wide variety of consumer andindustrial products, for example, plumbing fixtures, electrical boxes,automotive parts, and insulation for wire and cable.

Some parts made from poly(phenylene ether)-based compositions requirehigh flame retardancy. Examples include fuser holders forelectrophotographic copiers, fan blades, battery parts for hybrid andelectric vehicles, parts for automotive kinetic energy recovery systems,and electric vehicle junction boxes. Poly(phenylene ether) is inherentlyflame retardant, but it is often blended with other components, such asimpact modifiers and flow promoters, that reduce the flame retardancy ofthe resulting composition even as they improve its processing andmechanical properties. So, flame retardant additives are often requiredfor blends of poly(phenylene ether)s with these other components.

Some molded parts require a flammability rating of V-0 in the 20millimeter Vertical Burning Flame Test of Underwriter's LaboratoryBulletin 94 “Tests for Flammability of Plastic Materials, UL 94”. ThisV-0 rating can be difficult to achieve in a poly(phenylene ether)composition, even when flame retardant concentration is increased, andconcentrations of flammable components are decreased. And when the V-0rating is achievable, it often comes at the expense of diminished heatresistance and diminished stiffness.

There remains a need for poly(phenylene ether)-containing parts thatexhibit a UL 94 V-0 rating while maintaining high heat resistance andstiffness.

BRIEF SUMMARY OF EMBODIMENTS OF THE INVENTION

One embodiment is an article comprising a composition, wherein thearticle is selected from the group consisting of fuser holders forelectrophotographic copiers, fan blades, battery parts for hybrid andelectric vehicles, parts for automotive kinetic energy recovery systems,and electric vehicle junction boxes; wherein the composition comprises0.5 to 85 weight percent of a poly(phenylene ether)-polysiloxanecopolymer comprising a poly(phenylene ether)-polysiloxane blockcopolymer, a poly(phenylene ether)-polysiloxane graft copolymer, or acombination thereof; 5 to 25 weight percent of a flame retardantcomprising an organophosphate ester, a phosphazene, or a combinationthereof; and 10 to 35 weight percent of a reinforcing filler; whereinall weight percent values are based on the total weight of thecomposition; provided that when the article is a fuser holder, thecomposition comprises 2 to 10 weight percent of a poly(phenyleneether)-polysiloxane block copolymer reaction product comprising the apoly(phenylene ether)-polysiloxane block copolymer and a first apoly(phenylene ether), and further comprises 55 to 75 weight percent ofa second poly(phenylene ether).

This and other embodiments are described in detail below.

DETAILED DESCRIPTION OF THE INVENTION

The present inventors have determined that parts (also referred toherein as “articles”) fabricated from a composition containing specificamounts of a poly(phenylene ether)-polysiloxane copolymer, a flameretardant, and a reinforcing filler exhibit a UL 94 V-0 rating whilemaintaining high heat resistance and stiffness. In some embodiments, thehigh heat resistance is manifested as a heat deflection temperature of110 to 180° C., specifically 130 to 170° C., determined according toASTM D 648-07 using 6.4 millimeter thick bars, an edgewise testdirection, a support span of 100 millimeters (Method B), a stress of1.82 megapascals, a deflection of 0.25 millimeters at reading, and aheating rate of 2° C./minute. In some embodiments, the high stiffness ismanifested as a flexural modulus of 3,500 to 7,000 megapascals,specifically 4,500 to 6,500 megapascals, determined at 23° C. accordingto ASTM D 790-07e1 using 6.4 millimeter thick bars, a support span of101.6 millimeters, and a test speed of 2.54 millimeters/minute. In someembodiments, the composition exhibits high melt flow, which facilitatesinjection molding of parts. The high melt flow can be objectivelymanifested as a melt volume flow rate of 10 to 30 cubic centimeters per10 minutes, specifically 10 to 25 cubic centimeters per 10 minutes,determined according to ASTM D 1238-04 at 300° C. using a load of 5kilograms, automatic timing (Procedure B), a capillary diameter of2.0955 millimeters, and a capillary length of 8.00 millimeters.

Examples of articles benefiting from the flame retardancy, heatresistance, and stiffness of the composition include fuser holders forelectrophotographic copiers (including fuser gates, fuser covers, andfuser frames), fan blades (including blades in fans employed in computerand telecommunication equipment such as personal computers, servers,routers, and base stations; blades in fans employed in businessequipment such as printers, copiers, faxes, and projectors; blades infans employed in electrical appliances such as refrigerators, freezers,washing machines and driers, microwave ovens, dishwashers, airconditioners, and audiovisual equipment; and blades in fans used inindustrial equipment, including robots), battery parts for hybrid andelectric vehicles (including battery cases, battery module cases,battery terminal blocks, battery spacers, and battery trays), parts forautomotive kinetic energy recovery systems (including battery modulecases and capacitor cases), and electric vehicle junction boxes.

The composition comprises a poly(phenylene ether)-polysiloxane copolymerthat comprises a poly(phenylene ether)-polysiloxane block copolymer, apoly(phenylene ether)-polysiloxane graft copolymer, or a combinationthereof.

In some embodiments, the composition comprises a poly(phenyleneether)-polysiloxane copolymer. The poly(phenylene ether)-polysiloxaneblock copolymer comprises a poly(phenylene ether) block and apolysiloxane block. Included in poly(phenylene ether)-polysiloxane blockcopolymers are diblock copolymers comprising one poly(phenylene ether)block and one polysiloxane block; triblock copolymers comprising twopoly(phenylene ether) blocks and one polysiloxane block, or onepoly(phenylene ether) block and two polysiloxane blocks; and multiblockcopolymers comprising at least two poly(phenylene ether) blocks and atleast two polysiloxane blocks.

Poly(phenylene ether)-polysiloxane diblock and triblock copolymers canbe synthesized by oxidative polymerization of a mixture of monohydricphenol and hydroxyaryl-terminated polysiloxane. This oxidativepolymerization produces a poly(phenylene ether)-polysiloxane blockcopolymer reaction product that comprises poly(phenyleneether)-polysiloxane block copolymer as the desired product andpoly(phenylene ether) as a by-product. This poly(phenylene ether)present in the reaction product is sometimes referred to herein as the“first poly(phenylene ether)” to distinguish it from a “secondpoly(phenylene ether)” that is optionally present in the composition andnot derived from the poly(phenylene ether)-polysiloxane block copolymerreaction product. It is unnecessary to separate the first poly(phenyleneether) from the poly(phenylene ether)-polysiloxane block copolymer. Thepoly(phenylene ether)-polysiloxane block copolymer can therefore beincorporated into the present composition as the poly(phenyleneether)-polysiloxane block copolymer reaction product that comprises thefirst poly(phenylene ether) in addition to the poly(phenyleneether)-polysiloxane block copolymer.

When the poly(phenylene ether)-polysiloxane block copolymer issynthesized by oxidative polymerization of a mixture of monohydricphenol and hydroxyaryl-terminated polysiloxane, the poly(phenyleneether) block is a polymerization product of the monohydric phenol.

In some embodiments, the monohydric phenol has the structure

and the poly(phenylene ether) block comprises phenylene ether repeatunits having the structure

wherein for each repeating unit, each Z¹ is independently unsubstitutedor substituted C₁-C₁₂ hydrocarbylthio, unsubstituted or substitutedC₁-C₁₂ hydrocarbyloxy, or unsubstituted or substituted C₁-C₁₂hydrocarbyl provided that the hydrocarbyl group is not tertiaryhydrocarbyl; and each Z² is independently hydrogen, unsubstituted orsubstituted C₁-C₁₂ hydrocarbylthio, unsubstituted or substituted C₁-C₁₂hydrocarbyloxy, or unsubstituted or substituted C₁-C₁₂ hydrocarbylprovided that the hydrocarbyl group is not tertiary hydrocarbyl. As usedherein, the term “hydrocarbyl”, whether used by itself, or as a prefix,suffix, or fragment of another term, refers to a residue that containsonly carbon and hydrogen. The residue can be aliphatic or aromatic,straight-chain, cyclic, bicyclic, branched, saturated, or unsaturated.It can also contain combinations of aliphatic, aromatic, straight chain,cyclic, bicyclic, branched, saturated, and unsaturated hydrocarbonmoieties. However, when the hydrocarbyl residue is described assubstituted, it may, optionally, contain heteroatoms over and above thecarbon and hydrogen members of the substituent residue. For example,when described as substituted, the hydrocarbyl residue can also containone or more carbonyl groups, amino groups, hydroxyl groups, or it cancontain heteroatoms within the backbone of the hydrocarbyl residue. Asone example, Z¹ of the phenylene ether repeat unit can be adi-n-butylaminomethyl group formed by reaction of a terminal3,5-dimethyl-1,4-phenyl group with the di-n-butylamine component of anoxidative polymerization catalyst. In some embodiments, the monohydricphenol comprises 2,6-dimethylphenol, 2,3,6-trimethylphenol, or acombination thereof, and the poly(phenylene ether) block comprises,respectfully, 2,6-dimethyl-1,4-phenylene ether repeat units, that is,repeat units having the structure

2,3,6-trimethyl-1,4-phenylene ether repeat units, or a combinationthereof

When the poly(phenylene ether)-polysiloxane block copolymer issynthesized by oxidative polymerization of a mixture of monohydricphenol and hydroxyaryl-terminated polysiloxane, the polysiloxane blockis a residue of the hydroxyaryl-terminated polysiloxane. In someembodiments, the polysiloxane block comprises repeat units having thestructure

wherein each occurrence of R¹ and R² is independently hydrogen or C₁-C₁₂hydrocarbyl; and the polysiloxane block further comprises a terminalunit having the structure

wherein Y is hydrogen, C₁-C₁₂ hydrocarbyl, or C₁-C₁₂ hydrocarbyloxy, andwherein each occurrence of R³ and R⁴ is independently hydrogen or C₁-C₁₂hydrocarbyl. In some embodiments, the polysiloxane repeat units comprisedimethylsiloxane (—Si(CH₃)₂O—) units. In some embodiments, thepolysiloxane block has the structure

wherein n is 20 to 60.

In a very specific embodiment, the poly(phenylene ether)-polysiloxaneblock copolymer comprises a poly(phenylene ether) block comprisingphenylene ether repeat units having the structure

anda polysiloxane block having the structure

wherein n is 30 to 60.

The hydroxyaryl-terminated polysiloxane comprises at least onehydroxyaryl terminal group. In some embodiments, thehydroxyaryl-terminated polysiloxane has a single hydroxyaryl terminalgroup, in which case a poly(phenylene ether)-polysiloxane diblockcopolymer is formed. In other embodiments, the hydroxyaryl-terminatedpolysiloxane has two hydroxyaryl terminal groups, in which case in whichcase poly(phenylene ether)-polysiloxane diblock copolymer and/orpoly(phenylene ether)-polysiloxane-poly(phenylene ether) triblockcopolymer are formed. It is also possible for the hydroxyaryl-terminatedpolysiloxane to have a branched structure that allows three or morehydroxyaryl terminal groups and the formation of corresponding branchedblock copolymers.

In a very specific procedure for preparing the poly(phenyleneether)-polysiloxane block copolymer reaction product, the monohydricphenol is 2,6-dimethylphenol; the hydroxyaryl-terminated polysiloxane isa eugenol-capped polydimethylsiloxane comprising 35 to 60dimethylsiloxane units; the oxidative copolymerization is conducted witha reaction time of 170 to 220 minutes; and the hydroxyaryl-terminatedpolysiloxane constitutes 2 to 7 weight percent of the combined weight ofthe monohydric phenol and the hydroxyaryl-terminated polysiloxane.

In some embodiments, the hydroxyaryl-terminated polysiloxane comprises20 to 80 siloxane repeat units, specifically 25 to 70 siloxane repeatunits, more specifically 30 to 60 siloxane repeat units, still morespecifically 35 to 50 siloxane repeat units, yet more specifically 40 to50 siloxane repeat units. The number of siloxane repeat units in thepolysiloxane block is essentially unaffected by the copolymerization andisolation conditions, and it is therefore equivalent to the number ofsiloxane repeat units in the hydroxyaryl-terminated polysiloxanestarting material. When not otherwise known, the average number ofsiloxane repeat units per hydroxyaryl-terminated polysiloxane moleculecan be determined by nuclear magnetic resonance (NMR) methods thatcompare the intensities of signals associated with the siloxane repeatunits to those associated with the hydroxyaryl terminal groups. Forexample, when the hydroxyaryl-terminated polysiloxane is aeugenol-capped polydimethylsiloxane, it is possible to determine theaverage number of siloxane repeat units by a proton nuclear magneticresonance (¹H NMR) method in which integrals for the protons of thedimethylsiloxane resonance and the protons of the eugenol methoxy groupare compared.

In some embodiments, the poly(phenylene ether)-polysiloxane blockcopolymer reaction product has a weight average molecular weight of atleast 30,000 atomic mass units. For example, the reaction product canhave a weight average molecular weight of 30,000 to 150,000 atomic massunits, specifically 35,000 to 120,000 atomic mass units, morespecifically 40,000 to 90,000 atomic mass units, even more specifically45,000 to 70,000 atomic mass units. In some embodiments, thepoly(phenylene ether)-polysiloxane block copolymer reaction product hasa number average molecular weight of 10,000 to 50,000 atomic mass units,specifically 10,000 to 30,000 atomic mass units, more specifically14,000 to 24,000 atomic mass units.

In some embodiments, the poly(phenylene ether)-polysiloxane blockcopolymer reaction product has an intrinsic viscosity of at least 0.3deciliter per gram, as measured by Ubbelohde viscometer at 25° C. inchloroform. In some embodiments, the intrinsic viscosity is 0.3 to 0.5deciliter per gram, specifically 0.31 to 0.5 deciliter per gram, morespecifically 0.35 to 0.47 deciliter per gram.

One indication of the efficiency with which the hydroxyaryl-terminatedpolysiloxane is incorporated into block copolymer is the lowconcentration of so-called poly(phenylene ether) “tail” groups in thereaction product. In a homopolymerization of 2,6-dimethylphenol, a largefraction of product molecules have a so-called head-to-tail structure inwhich the linear product molecule is terminated on one end by a3,5-dimethyl-4-hydroxyphenyl “head” and on the other end by a2,6-dimethylphenoxy “tail”. Thus, when the monohydric phenol consists of2,6-dimethylphenol, the poly(phenylene ether) tail group has thestructure

Note that the term “2,6-dimethylphenoxy” refers to a monovalent groupand does not encompass divalent 2,6-dimethyl-1,4-phenylene ether groups.In a copolymerization of monohydric phenol with hydroxyaryl-terminatedpolysiloxane, incorporation of the hydroxyaryl-terminated polysiloxaneinto block copolymer will reduce the concentration of phenylene ether“tail” groups. Thus, in some embodiments, the monohydric phenol consistsof 2,6-dimethylphenol, and the reaction product of comprises less thanor equal to 0.4 weight percent, specifically 0.1 to 0.4 weight percent,of 2,6-dimethylphenoxy groups, based on the weight of the reactionproduct. The low concentration of 2,6-dimethylphenoxy tail end groups isan indication that the reaction product comprises a reducedconcentration of the 2,6-dimethylphenol homopolymer and an increasedconcentration of the desired poly(phenylene ether)-polysiloxane blockcopolymer.

The poly(phenylene ether)-polysiloxane block copolymer reaction productcan further include groups derived from a diphenoquinone, which isitself an oxidation product of the monohydric phenol. For example, whenthe monohydric phenol is 2,6-dimethylphenol, the diphenoquinone is3,3′,5,5′-tetramethyl-4,4′-diphenoquinone. During the build phase of thecopolymerization, the diphenoquinone is typically incorporated into the“tail” end of a head-to-tail poly(phenylene ether) as the correspondingbiphenyl group. Through further reactions, the terminal biphenyl groupcan become an internal biphenyl group in the first poly(phenylene ether)chain. In some embodiments, the monohydric phenol consists of2,6-dimethylphenol, and the reaction product comprises 0.1 to 2.0 weightpercent, and specifically 1.1 to 2.0 weight percent, of2,6-dimethyl-4-(3,5-dimethyl-4-hydroxyphenyl)-phenoxy (“biphenyl”)groups. The biphenyl groups are present only in bifunctional(head-to-head or hydroxyl-diterminated) structure. So, the lowconcentration of biphenyl group is an indication that the reactionproduct comprises a reduced concentration of such bifunctional2,6-dimethylphenol homopolymer and an increased concentration of thedesired poly(phenylene ether)-polysiloxane block copolymer.

The poly(phenylene ether)-polysiloxane block copolymer content of apoly(phenylene ether)-polysiloxane block copolymer reaction product canbe estimated by nuclear magnetic resonance spectroscopy (NMR). Forexample, when the monohydric phenol is 2,6-dimethylphenol, and thehydroxylaryl-terminated polysiloxane is a eugenol-diterminatedpolydimethylsiloxane, the reaction product can be approximated as amixture of head-to-tail poly(phenylene ether) homopolymer, head-to-headpoly(phenylene ether) homopolymer (incorporating a biphenyl group), andpoly(phenylene ether)-polysiloxane-poly(phenylene ether) triblockcopolymer. Nuclear magnetic resonance analysis of the mixture can beused to determine the relative concentrations of “head groups” havingthe structure

“tail groups” having the structure

and“biphenyl groups” having the structure

The concentration of poly(phenylene ether)-polysiloxane-poly(phenyleneether) triblock copolymer (PSP) can then be calculated as

PSP=½([head groups]−[tail groups]−2[biphenyl groups]).

In some embodiments, the poly(phenylene ether)-polysiloxane blockcopolymer reaction product incorporates greater than 75 weight percent,of the hydroxyaryl-terminated polysiloxane starting material into thepoly(phenylene ether)-polysiloxane block copolymer. Specifically, theamount of the hydroxyaryl-terminated polysiloxane incorporated into thepoly(phenylene ether)-polysiloxane block copolymer can be at least 80weight percent, more specifically at least 85 weight percent, still morespecifically at least 90 weight percent, yet more specifically at least95 weight percent.

Details relating to the preparation, characterization, and properties ofthe poly(phenylene ether)-polysiloxane block copolymer reaction productcan be found in U.S. Pat. Nos. 8,017,697, 8,669,332, and 8,722,837 toCarrillo et al.

In addition to the oxidative copolymerization method described above, apolyesterification method can be used to form the poly(phenyleneether)-polysiloxane block copolymer. When the polyesterification methodis used, the product is a multiblock copolymer comprising at least twopoly(phenylene ether) blocks and at least two polysiloxane blocks. Thus,in some embodiments, the poly(phenylene ether)-polysiloxane blockcopolymer comprises a poly(phenylene ether)-polysiloxane multiblockcopolymer that is the product of copolymerizing a hydroxy-diterminatedpoly(phenylene ether), a hydroxyaryl-diterminated polysiloxane, and anaromatic diacid chloride.

The hydroxy-diterminated poly(phenylene ether) can have the structure

wherein x and y are each independently 0 to about 100, provided that thesum of x and y is at least 2; each occurrence of Q¹ is independentselected from the group consisting of halogen, unsubstituted orsubstituted C₁-C₁₂ hydrocarbylthio, unsubstituted or substituted C₁-C₁₂hydrocarbyloxy, unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxywherein at least two carbon atoms separate the halogen and oxygen atoms,and unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that thehydrocarbyl group is not tertiary hydrocarbyl; each occurrence of Q² isindependently selected from the group consisting of hydrogen, halogen,C₁-C₁₂ hydrocarbylthio, C₁-C₁₂ hydrocarbyloxy, C₂-C₁₂ halohydrocarbyloxywherein at least two carbon atoms separate the halogen and oxygen atoms,and unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that thehydrocarbyl group is not tertiary hydrocarbyl; and L has the structure

wherein each occurrence of R⁵ and R⁶ is independently selected from thegroup consisting of hydrogen, halogen, unsubstituted or substitutedC₁-C₁₂ hydrocarbylthio, unsubstituted or substituted C₁-C₁₂hydrocarbyloxy, unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxywherein at least two carbon atoms separate the halogen and oxygen atoms,and unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that thehydrocarbyl group is not tertiary hydrocarbyl; z is 0 or 1; and Y has astructure selected from the group consisting of

wherein each occurrence of R⁷-R¹⁰ is independently hydrogen or C₁-C₁₂hydrocarbyl.

In some embodiments, the hydroxy-diterminated poly(phenylene ether) hasthe structure

wherein each occurrence of Q³ is independently methyl ordi-n-butylaminomethyl; and each occurrence of a and b is independently 0to about 100, provided that the sum of a and b is 3 to 100. In someembodiments, the sum of a and b is 4 to 30.

The aromatic diacid chloride used in the polyesterification method canbe, for example, terephthaloyl chloride, isophthaloyl chloride,4,4′-biphenyldicarbonyl chloride, 3,3′-biphenyldicarbonyl chloride,3,4′-biphenyldicarbonyl chloride, 4,4′-oxybis(benzoyl chloride),3,3′-oxybis(benzoyl chloride), 3,4′-oxybis(benzoyl chloride),4,4′-sulfonylbis(benzoyl chloride), 3,3′-sulfonylbis(benzoyl chloride),3,4′-sulfonylbis(benzoyl chloride), naphthalene-2,6-dicarbonyl chloride,or a mixture thereof. In some embodiments, the aromatic diacid chloridecomprises terephthaloyl chloride.

As noted above, when the poly(phenylene ether)-polysiloxane multiblockcopolymer is prepared by the polyesterification method, it comprises atleast two poly(phenylene ether) blocks and at least two polysiloxaneblocks. However, it can contain many more of each type of block. Forexample, in some embodiments, the poly(phenylene ether)-polysiloxanemultiblock copolymer comprises about 5 to about 25 poly(phenylene ether)blocks and about 10 to about 30 polysiloxane blocks.

Additional details relating to the polyesterification method and thepoly(phenylene ether)-polysiloxane multiblock copolymer prepared therebycan be found in U.S. Pat. No. 8,309,665 B2 to Kamalakaran et al. Analternative method of forming poly(phenylene ether)-polysiloxanemultiblock copolymers is described in Cella et al.,

The poly(phenylene ether)-polysiloxane copolymer can include apoly(phenylene ether)-polysiloxane graft copolymer. A poly(phenyleneether)-polysiloxane graft copolymer comprises a poly(phenylene ether)backbone and at least one polysiloxane graft at an internal (notterminal) phenylene ether unit of the poly(phenylene ether) backbone.Poly(phenylene ether)-polysiloxane graft copolymers can be prepared byoxidative copolymerization of a monohydric phenol, as defined above, anda phenol-polysiloxane macromer having the structure

wherein R¹¹ is halogen, unsubstituted or substituted C₁-C₁₂hydrocarbylthio, unsubstituted or substituted C₁-C₁₂ hydrocarbyloxy,unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxy wherein at leasttwo carbon atoms separate the halogen and oxygen atoms, or unsubstitutedor substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group isnot tertiary hydrocarbyl; R¹² is hydrogen, halogen, unsubstituted orsubstituted C₁-C₁₂ hydrocarbylthio, unsubstituted or substituted C₁-C₁₂hydrocarbyloxy, unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxywherein at least two carbon atoms separate the halogen and oxygen atoms,or unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that thehydrocarbyl group is not tertiary hydrocarbyl; R¹³ is C₂-C₂₀hydrocarbylene; each occurrence of R¹⁴ is independently hydrogen orC₁-C₁₂ hydrocarbyl; R¹⁵ is C₁-C₁₂ hydrocarbyl; and m is 3 to 100. In aspecific embodiment, the monohydric phenol is 2,6-dimethylphenol, and inthe phenol-polysiloxane macromer, R¹¹ is methyl, R¹² is hydrogen, R¹³ istrimethylene (—CH₂—CH₂—CH₂—), each occurrence of R¹⁴ is methyl, R¹⁵ ismethyl, and m is 20 to 60. In some embodiments, the molar ratio ofmonohydric phenol to phenol-polysiloxane macromere is 10:1 to 1000:1,specifically 20:1 to 100:1 during the oxidative copolymerization. Insome embodiments, the weight percent siloxane in the poly(phenyleneether)-polysiloxane graft copolymer is 0.5 to 10 weight percent,specifically 1 to 8 weight percent. Additional details relating topoly(phenylene ether)-polysiloxane graft copolymers prepared byoxidative copolymerization can be found in U.S. Pat. No. 5,281,686 toBlohm et al. Poly(phenylene ether)-polysiloxane graft copolymers canalso be prepared by redistribution of a poly(phenylene ether) in thepresence of a hydroxyaryl-terminated polysiloxane. This procedure isdescribed in U.S. Pat. No. 5,596,048 to Blohm et al.

The composition can comprise a mixture of a poly(phenyleneether)-polysiloxane block copolymer and a poly(phenyleneether)-polysiloxane graft copolymer.

In some embodiments, the composition comprises 0.025 to 5 weight percentof polysiloxane covalently bound in the poly(phenyleneether)-polysiloxane copolymer. In other words, the poly(phenyleneether)-polysiloxane copolymer contributes 0.025 to 5 weight percent ofpolysiloxane to the composition as a whole. In some embodiments, thecovalently bound polysiloxane amount is 0.025 to 2 weight percent,specifically 0.05 to 1 weight percent, based on the total weight of thecomposition. In other embodiments, the covalently bound polysiloxaneamount is 1 to 6 weight percent, specifically 2 to 4 weight percent,based on the total weight of the composition. In some embodiments, thepolysiloxane content of the composition consists essentially ofpolysiloxane that has been incorporated into the poly(phenyleneether)-polysiloxane copolymer. In some embodiments, the poly(phenyleneether)-polysiloxane copolymer comprises 1 to 8 weight percent siloxanerepeat units and 12 to 99 weight percent phenylene ether repeat units,based on the total weight of the poly(phenylene ether)-polysiloxanecopolymer. Within these ranges, the amount of siloxane repeat units canbe 2 to 7 weight percent, specifically 3 to 6 weight percent, morespecifically 4 to 5 weight percent; and the amount of phenylene etherrepeat units can be 93 to 98 weight percent, specifically 94 to 97weight percent, more specifically 95 to 96 weight percent.

The poly(phenylene ether)-polysiloxane copolymer can include relativelysmall amounts of very low molecular weight species. Thus, in someembodiments, the poly(phenylene ether)-polysiloxane copolymer comprisesless than 25 weight percent of molecules having a molecular weight lessthan 10,000 atomic mass units, specifically 5 to 25 weight percent ofmolecules having a molecular weight less than 10,000 atomic mass units,more specifically 7 to 21 weight percent of molecules having a molecularweight less than 10,000 atomic mass units. In some embodiments, themolecules having a molecular weight less than 10,000 atomic mass unitscomprise 5 to 10 weight percent siloxane repeat units, specifically 6 to9 weight percent siloxane repeat units.

Similarly, the poly(phenylene ether)-polysiloxane copolymer can alsoinclude relatively small amounts of very high molecular weight species.Thus, in some embodiments, the poly(phenylene ether)-polysiloxanecopolymer comprises less than 25 weight percent of molecules having amolecular weight greater than 100,000 atomic mass units, specifically 5to 25 weight percent of molecules having a molecular weight greater than100,000 atomic mass units, more specifically 7 to 23 weight percent ofmolecules having a molecular weight greater than 100,000 atomic massunits. In some embodiments, the molecules having a molecular weightgreater than 100,000 atomic mass units comprise 3 to 6 weight percentsiloxane repeat units, specifically 4 to 5 weight percent siloxanerepeat units.

The composition comprises 0.5 to 85 weight percent of the poly(phenyleneether)-polysiloxane copolymer, based on the total weight of thecomposition. In some embodiments, the poly(phenylene ether)-polysiloxanecopolymer amount is 1 to 20 weight percent, specifically 2 to 10 weightpercent. In other embodiments, the poly(phenylene ether)-polysiloxanecopolymer amount is 30 to 85 weight percent, specifically 40 to 75weight percent, more specifically 53 to 63 weight percent.

In some embodiments, particularly those in which the amount of thepoly(phenylene ether)-polysiloxane copolymer is less than 50 weightpercent, it can be beneficial to include a second poly(phenylene ether)in the composition. As used herein, the term “second poly(phenyleneether)” refers to a poly(phenylene ether) that is not derived from thepoly(phenylene ether)-polysiloxane block copolymer reaction. The secondpoly(phenylene ether) can be chemically the same as or different fromthe first poly(phenylene ether). Suitable first and secondpoly(phenylene ether)s include those comprising repeating structuralunits having the formula

wherein each occurrence of Z¹ is independently halogen, unsubstituted orsubstituted C₁-C₁₂ hydrocarbylthio, unsubstituted or substituted C₁-C₁₂hydrocarbyloxy, unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxywherein at least two carbon atoms separate the halogen and oxygen atoms,or unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that thehydrocarbyl group is not tertiary hydrocarbyl; and each occurrence of Z²is independently hydrogen, halogen, unsubstituted or substituted C₁-C₁₂hydrocarbylthio, unsubstituted or substituted C₁-C₁₂ hydrocarbyloxy,unsubstituted or substituted C₂-C₁₂ halohydrocarbyloxy wherein at leasttwo carbon atoms separate the halogen and oxygen atoms, or unsubstitutedor substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group isnot tertiary hydrocarbyl.

In some embodiments, the second poly(phenylene ether) has an intrinsicviscosity of 0.2 to 1 deciliter per gram measured by Ubbelohdeviscometer at 25° C. in chloroform. Within this range, the secondpoly(phenylene ether) intrinsic viscosity can be 0.2 to 0.5 deciliterper gram, specifically 0.2 to 0.4 deciliter per gram, still morespecifically 0.25 to 0.35 deciliter per gram.

In some embodiments, the second poly(phenylene ether) comprises2,6-dimethyl-1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenyleneether units, or a combination thereof. In some embodiments, the secondpoly(phenylene ether) comprises a poly(2,6-dimethyl-1,4-phenyleneether). In some embodiments, the second poly(phenylene ether) comprisesa poly(2,6-dimethyl-1,4-phenylene ether) having an intrinsic viscosityof 0.2 to 0.4 deciliter per gram, specifically 0.25 to 0.35 deciliterper gram, measured by Ubbelohde viscometer at 25° C. in chloroform.

When present, the second poly(phenylene ether) can be used in an amountof 5 to 84.5 weight percent, specifically 20 to 80 weight percent, morespecifically 55 to 75 weight percent, based on the total weight of thecomposition.

In addition to the poly(phenylene ether)-polysiloxane copolymer and theoptional second poly(phenylene ether), the composition comprises a flameretardant. The flame retardant comprises an organophosphate ester, aphosphazene, or a combination thereof.

In some embodiments, the flame retardant comprises an organophosphateester. Exemplary organophosphate ester flame retardants includephosphate esters comprising phenyl groups, substituted phenyl groups, ora combination of phenyl groups and substituted phenyl groups, bis(arylphosphate) esters based upon resorcinol such as, for example, resorcinolbis(diphenyl phosphate), as well as those based upon bisphenols such as,for example, bisphenol A bis(diphenyl phosphate). In some embodiments,the organophosphate ester is selected from tris(alkylphenyl) phosphates(for example, CAS Reg. No. 89492-23-9 or CAS Reg. No. 78-33-1),resorcinol bis(diphenyl phosphate) (CAS Reg. No. 57583-54-7), bisphenolA bis(diphenyl phosphate) (CAS Reg. No. 181028-79-5), triphenylphosphate (CAS Reg. No. 115-86-6), tris(isopropylphenyl) phosphates (forexample, CAS Reg. No. 68937-41-7), and combinations thereof.

In some embodiments the organophosphate ester comprises a bis(arylphosphate) having the formula

wherein R is independently at each occurrence a C₁-C₁₂ alkylene group;R²⁰ and R²¹ are independently at each occurrence a C₁-C₅ alkyl group;R¹⁶, R¹⁷, and R¹⁹ are independently a C₁-C₁₂ hydrocarbyl group; R¹⁸ isindependently at each occurrence a C₁-C₁₂ hydrocarbyl group; n is 1 to25; and s1 and s2 are independently an integer equal to 0, 1, or 2. Insome embodiments OR¹⁶, OR¹⁷, OR¹⁸ and OR¹⁹ are independently derivedfrom phenol, a monoalkylphenol, a dialkylphenol, or a trialkylphenol.

As readily appreciated by one of ordinary skill in the art, the bis(arylphosphate) is derived from a bisphenol. Exemplary bisphenols include2,2-bis(4-hydroxyphenyl)propane (bisphenol A),2,2-bis(4-hydroxy-3-methylphenyl)propane, bis(4-hydroxyphenyl)methane,bis(4-hydroxy-3,5-dimethylphenyl)methane and1,1-bis(4-hydroxypheny)ethane. In some embodiments, the bisphenolcomprises bisphenol A.

In some embodiments, the flame retardant comprises a phosphazene. Aphosphazene is a compound comprising repeat units having the structure

wherein each occurrence of R²² is independently C₁-C₆ alkoxy,unsubstituted or substituted phenoxy, or unsubstituted or substitutednaphthyloxy. When present, the substituents on the phenoxy ornaphthyloxy groups can be, for example, C₁-C₆ alkyl, C₁-C₆ alkoxy, orphenyl.

In some embodiments, the phosphazene comprises a cyclic oligophosphazenehaving the structure

wherein R²² is defined above and a is 3 to 12, specifically 3 to 6. Insome embodiments, a is 3 and each occurrence of R²² is unsubstitutedphenoxy.

In some embodiments, the phosphazene comprises a linear oligophosphazeneor polyphosphazene having the structure

wherein R²² is defined above; b is 3 to 1,000; A is —N═P(O)(R²²) or—N═P(R²²)₃; and B is —P(R²²)₄ or —P(O)(R²²)₂.

The phosphazene can be a crosslinked polyphosphazene comprising aphenylene group, a biphenylene group, or a group having the structure

wherein X is C₁-C₆ alkylidene, O, S, or SO₂. This crosslinking group istypically directly bonded at each end to a phosphazene phosphorus atom.

A mixture of at least two of cyclic oligophosphazenes, linearoligophosphazenes, linear polyphosphazenes, and crosslinked phosphazenescan be used. In some embodiments, the phosphazene comprises at last 80weight percent cyclic phosphazenes, based on the weight of thephosphazene.

Methods for making phosphazenes are known, and phosphazenes arecommercially available as, for example, RABITLE™ FP-100 and RABITLE™FP-110 from Fushimi Pharmaceutical Co., Ltd.; and IDB-Poretar-201 fromID-Biochem, and SPB-100 from Otsuka Chemical Company.

In addition to the organophosphate ester, the phosphazene, or thecombination thereof, the flame retardant can, optionally, furthercomprise a metal dialkylphosphinate, a nitrogen-containing flameretardant, a metal hydroxide, or a combination thereof.

As used herein, the term “metal dialkylphosphinate” refers to a saltcomprising at least one metal cation and at least one dialkylphosphinateanion. In some embodiments, the metal dialkylphosphinate has the formula

wherein R^(a) and R^(b) are each independently C₁-C₆ alkyl; M iscalcium, magnesium, aluminum, or zinc; and d is 2 or 3. Examples ofR^(a) and R^(b) include methyl, ethyl, n-propyl, isopropyl, n-butyl,tert-butyl, and n-pentyl. In some embodiments, R^(a) and R^(b) areethyl, M is aluminum, and d is 3 (that is, the metal dialkylphosphinateis aluminum tris(diethylphosphinate)).

In some embodiments, the metal dialkylphosphinate is in particulateform. The metal dialkylphosphinate particles may have a median particlediameter (D50) less than or equal to 40 micrometers, or, morespecifically, a D50 less than or equal to 30 micrometers, or, even morespecifically, a D50 less than or equal to 25 micrometers. Additionally,the metal dialkylphosphinate may be combined with a polymer, such as thepoly(phenylene ether)-polysiloxane block copolymer reaction product, theoptional second poly(phenylene ether), or the optional impact modifier,to form a masterbatch. The metal dialkylphosphinate masterbatchcomprises the metal dialkylphosphinate in an amount greater than ispresent in the thermoplastic composition. Employing a masterbatch forthe addition of the metal dialkylphosphinate to the other components ofthe composition can facilitate addition and improve distribution of themetal dialkylphosphinate.

Nitrogen-containing flame retardants include those comprising anitrogen-containing heterocyclic base and a phosphate or pyrophosphateor polyphosphate acid. In some embodiments, the nitrogen-containingflame retardant has the formula

wherein g is 1 to 10,000, and the ratio of f to g is 0.5:1 to 1.7:1,specifically 0.7:1 to 1.3:1, more specifically 0.9:1 to 1.1:1. It willbe understood that this formula includes species in which one or moreprotons are transferred from the phosphate group(s) to the melaminegroup(s). When g is 1, the nitrogen-containing flame retardant ismelamine phosphate (CAS Reg. No. 20208-95-1). When g is 2, thenitrogen-containing flame retardant is melamine pyrophosphate (CAS Reg.No. 15541 60-3). When g is, on average, greater than 2, thenitrogen-containing flame retardant is a melamine polyphosphate (CASReg. No. 56386-64-2). In some embodiments, the nitrogen-containing flameretardant is melamine pyrophosphate, melamine polyphosphate, or amixture thereof. In some embodiments in which the nitrogen-containingflame retardant is melamine polyphosphate, g has an average value ofgreater than 2 to 10,000, specifically 5 to 1,000, more specifically 10to 500. In some embodiments in which the nitrogen-containing flameretardant is melamine polyphosphate, g has an average value of greaterthan 2 to 500. Methods for preparing melamine phosphate, melaminepyrophosphate, and melamine polyphosphate are known in the art, and allare commercially available. For example, melamine polyphosphates may beprepared by reacting polyphosphoric acid and melamine, as described, forexample, in U.S. Pat. No. 6,025,419 to Kasowski et al., or by heatingmelamine pyrophosphate under nitrogen at 290° C. to constant weight, asdescribed in U.S. Pat. No. 6,015,510 to Jacobson et al. In someembodiments, the nitrogen-containing flame retardant comprises melaminecyanurate.

The nitrogen-containing flame retardant can have a low volatility. Forexample, in some embodiments, the nitrogen-containing flame retardantexhibits less than 1 percent weight loss by thermogravimetric analysiswhen heated at a rate of 20° C. per minute from 25 to 280° C.,specifically 25 to 300° C., more specifically 25 to 320° C.

Suitable metal hydroxides include all those capable of providing fireretardancy, as well as combinations of such metal hydroxides. The metalhydroxide can be chosen to have substantially no decomposition duringprocessing of the fire additive composition and/or flame retardantthermoplastic composition. Substantially no decomposition is definedherein as amounts of decomposition that do not prevent the flameretardant additive composition from providing the desired level of fireretardancy. Exemplary metal hydroxides include, but are not limited to,magnesium hydroxide (for example, CAS Reg. No. 1309-42-8), aluminumhydroxide (for example, CAS Reg. No. 21645-51-2), cobalt hydroxide (forexample, CAS Reg. No. 21041-93-0), and combinations thereof. In someembodiments, the metal hydroxide comprises magnesium hydroxide. In someembodiments the metal hydroxide has an average particle size less thanor equal to 10 micrometers and/or a purity greater than or equal to 90weight percent. In some embodiments it is desirable for the metalhydroxide to contain substantially no water, for example as evidenced bya weight loss of less than 1 weight percent upon drying at 120° C. for 1hour. In some embodiments the metal hydroxide can be coated, forexample, with stearic acid or other fatty acid.

The amount of the flame retardant can be 5 to 25 weight percent, basedon the total weight of the composition. In some embodiments, the amountof the flame retardant is 5 to 20 weight percent, specifically 5 to 15weight percent. In other embodiments, the amount of the flame retardantis 10 to 25 weight percent, specifically 15 to 25 weight percent.

In addition to the poly(phenylene ether)-polysiloxane block copolymerreaction product, the optional second poly(phenylene ether), and theflame retardant, the composition comprises a reinforcing filler.Reinforcing fillers include, for example, glass fibers, carbon fibers,wollastonite, halloysite, clays, talcs, micas, glass flakes, solid glassbeads, hollow glass beads, solid ceramic beads, hollow ceramic beads,and combinations thereof. In some embodiments, the reinforcing fillercomprises or consists of glass fibers.

Suitable glass fibers include those based on E, A, C, ECR, R, S, D, andNE glasses, as well as quartz. In some embodiments, the glass fiber hasa diameter of 2 to 30 micrometers, specifically 5 to 25 micrometers,more specifically 10 to 15 micrometers. In some embodiments, the lengthof the glass fibers before compounding is 2 to 7 millimeters,specifically 3 to 5 millimeters. Suitable glass fiber is commerciallyavailable from suppliers including, for example, Owens Corning, NipponElectric Glass, PPG, and Johns Manville.

The reinforcing filler can, optionally, include an adhesion promoter toimprove its compatibility with the poly(phenylene ether)-polysiloxaneblock copolymer reaction product. Adhesion promoters include chromiumcomplexes, silanes, titanates, zircoaluminates, propylene maleicanhydride copolymers, reactive cellulose esters, and the like.

The reinforcing filler can be used in an amount of 10 to 35 weightpercent, based on the total weight of the composition. In someembodiments, the reinforcing filler amount is 10 to 25 weight percent,specifically 10 to 20 weight percent. In other embodiments, thereinforcing filler amount is 15 to 30 weight percent, specifically 15 to25 weight percent.

The composition can, optionally, further include an impact modifierImpact modifiers include, for example, rubber-modified polystyrenes,unhydrogenated block copolymers of an alkenyl aromatic monomer and aconjugated diene, hydrogenated block copolymers of an alkenyl aromaticmonomer and a conjugated diene, acrylate core-shell impact modifiers(e.g., those having a crosslinked poly(butyl acrylate) core and agrafted poly(methyl methacrylate) shell), and combinations thereof.

The impact modifier can include a rubber-modified polystyrene.Rubber-modified polystyrene comprises polystyrene and polybutadiene.Rubber-modified polystyrenes are sometimes referred to as “high-impactpolystyrenes” or “HIPS”. In some embodiments, the rubber-modifiedpolystyrene comprises 80 to 96 weight percent polystyrene, specifically88 to 94 weight percent polystyrene; and 4 to 20 weight percentpolybutadiene, specifically 6 to 12 weight percent polybutadiene, basedon the weight of the rubber-modified polystyrene. Suitablerubber-modified polystyrenes are commercially available as, for example,HIPS3190 from SABIC Innovative Plastics.

The impact modifier can include an unhydrogenated block copolymer of analkenyl aromatic compound and a conjugated diene. For brevity, thiscomponent is referred to as an “unhydrogenated block copolymer”. Theunhydrogenated block copolymer can comprise 10 to 90 weight percent ofpoly(alkenyl aromatic) content and 90 to 10 weight percent ofpoly(conjugated diene) content, based on the weight of theunhydrogenated block copolymer. In some embodiments, the unhydrogenatedblock copolymer is a low poly(alkenyl aromatic content) unhydrogenatedblock copolymer in which the poly(alkenyl aromatic) content is 10 toless than 40 weight percent, specifically 20 to 35 weight percent, morespecifically 25 to 35 weight percent, yet more specifically 30 to 35weight percent, all based on the weight of the low poly(alkenylaromatic) content unhydrogenated block copolymer. In other embodiments,the unhydrogenated block copolymer is a high poly(alkenyl aromatic)content unhydrogenated block copolymer in which the poly(alkenylaromatic) content is 40 to 90 weight percent, specifically 50 to 80weight percent, more specifically 60 to 70 weight percent, all based onthe weight of the high poly(alkenyl aromatic) content unhydrogenatedblock copolymer.

In some embodiments, the unhydrogenated block copolymer has a weightaverage molecular weight of 40,000 to 400,000 atomic mass units. Thenumber average molecular weight and the weight average molecular weightcan be determined by gel permeation chromatography and based oncomparison to polystyrene standards. In some embodiments, theunhydrogenated block copolymer has a weight average molecular weight of200,000 to 400,000 atomic mass units, specifically 220,000 to 350,000atomic mass units. In other embodiments, the unhydrogenated blockcopolymer has a weight average molecular weight of 40,000 to 200,000atomic mass units, specifically 40,000 to 180,000 atomic mass units,more specifically 40,000 to 150,000 atomic mass units.

The alkenyl aromatic monomer used to prepare the unhydrogenated blockcopolymer can have the structure

wherein R²³ and R²⁴ each independently represent a hydrogen atom, aC₁-C₈ alkyl group, or a C₂-C₈ alkenyl group; R²⁵ and R²⁹ eachindependently represent a hydrogen atom, a C₁-C₈ alkyl group, a chlorineatom, or a bromine atom; and R²⁶, R²⁷, and R²⁸ each independentlyrepresent a hydrogen atom, a C₁-C₈ alkyl group, or a C₂-C₈ alkenylgroup, or R²⁶ and R²⁷ are taken together with the central aromatic ringto form a naphthyl group, or R²⁷ and R²⁸ are taken together with thecentral aromatic ring to form a naphthyl group. Specific alkenylaromatic monomers include, for example, styrene, chlorostyrenes such asp-chlorostyrene, methylstyrenes such as alpha-methylstyrene andp-methylstyrene, and t-butylstyrenes such as 3-t-butylstyrene and4-t-butylstyrene. In some embodiments, the alkenyl aromatic monomer isstyrene.

The conjugated diene used to prepare the unhydrogenated block copolymercan be a C₄-C₂₀ conjugated diene. Suitable conjugated dienes include,for example, 1,3-butadiene, 2-methyl-1,3-butadiene,2-chloro-1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene,1,3-hexadiene, and combinations thereof. In some embodiments, theconjugated diene is 1,3-butadiene, 2-methyl-1,3-butadiene, or acombination thereof. In some embodiments, the conjugated diene consistsof 1,3-butadiene.

The unhydrogenated block copolymer is a copolymer comprising (A) atleast one block derived from an alkenyl aromatic compound and (B) atleast one block derived from a conjugated diene. The arrangement ofblocks (A) and (B) includes a linear structure, a grafted structure, anda radial teleblock structure with or without a branched chain. Linearblock copolymers include tapered linear structures and non-taperedlinear structures. In some embodiments, the unhydrogenated blockcopolymer has a tapered linear structure. In some embodiments, theunhydrogenated block copolymer has a non-tapered linear structure. Insome embodiments, the unhydrogenated block copolymer comprises a (B)block that comprises random incorporation of alkenyl aromatic monomer.Linear block copolymer structures include diblock (A-B block), triblock(A-B-A block or B-A-B block), tetrablock (A-B-A-B block), and pentablock(A-B-A-B-A block or B-A-B-A-B block) structures as well as linearstructures containing 6 or more blocks in total of (A) and (B), whereinthe molecular weight of each (A) block can be the same as or differentfrom that of other (A) blocks, and the molecular weight of each (B)block can be the same as or different from that of other (B) blocks. Insome embodiments, the unhydrogenated block copolymer is a diblockcopolymer, a triblock copolymer, or a combination thereof.

In some embodiments, the unhydrogenated block copolymer excludes theresidue of monomers other than the alkenyl aromatic compound and theconjugated diene. In some embodiments, the unhydrogenated blockcopolymer consists of blocks derived from the alkenyl aromatic compoundand the conjugated diene. It does not comprise grafts formed from theseor any other monomers. It also consists of carbon and hydrogen atoms andtherefore excludes heteroatoms.

In some embodiments, the unhydrogenated block copolymer includes theresidue of one or more acid functionalizing agents, such as maleicanhydride.

In some embodiments, the unhydrogenated block copolymer comprises apolystyrene-polybutadiene-polystyrene triblock copolymer. In someembodiments, the unhydrogenated block copolymer comprises apolystyrene-polyisoprene-polystyrene triblock copolymer.

Methods for preparing unhydrogenated block copolymers are known in theart and unhydrogenated block copolymers are commercially available.Illustrative commercially available unhydrogenated block copolymersinclude the polystyrene-polybutadiene-polystyrene triblock copolymersfrom Kraton Performance Polymers Inc. under the trade names Kraton™D1101 and D1102; and the styrene-butadiene radial teleblock copolymersfrom Chevron Phillips Chemical Company under the trade names K-RESIN™KK38, KR01, KR03, and KR05.

The impact modifier can be a hydrogenated block copolymer of an alkenylaromatic compound and a conjugated diene. For brevity, this component isreferred to as a “hydrogenated block copolymer”. The hydrogenated blockcopolymer is the same as the unhydrogenated block copolymer, except thatin the hydrogenated block copolymer the aliphatic unsaturated groupcontent in the block (B) derived from a conjugated diene has been atleast partially reduced by hydrogenation. In some embodiments, thealiphatic unsaturation in the (B) block is reduced by at least 50percent, specifically at least 70 percent, more specifically at least 90percent.

Illustrative commercially available hydrogenated block copolymersinclude the polystyrene-poly(ethylene-propylene) diblock copolymersavailable from Kraton Performance Polymers Inc. as KRATON™ G1701 andG1702; the polystyrene-poly(ethylene-butylene)-polystyrene triblockcopolymers available from Kraton Performance Polymers Inc. as KRATON™G1641, G1650, G1651, G1654, G1657, G1726, G4609, G4610, GRP-6598,MD-6932M, MD-6933, and MD-6939; thepolystyrene-poly(ethylene-propylene)-polystyrene triblock copolymersavailable from Kraton Performance Polymers Inc. as KRATON™ G1730; themaleic anhydride-grafted polystyrene-poly(ethylene-butylene)-polystyrenetriblock copolymers available from Kraton Performance Polymers Inc. asKRATON™ G1901, G1924, and MD-6684; the maleic anhydride-graftedpolystyrene-poly(ethylene-butylene-styrene)-polystyrene triblockcopolymer available from Kraton Performance Polymers Inc. as KRATON™MD-6670; the polystyrene-poly(ethylene-butylene)-polystyrene triblockcopolymer comprising 67 weight percent polystyrene available from AsahiKasei Elastomer as TUFTEC™ H1043; thepolystyrene-poly(ethylene-butylene)-polystyrene triblock copolymercomprising 42 weight percent polystyrene available from Asahi KaseiElastomer as TUFTEC™ H1051; thepolystyrene-poly(butadiene-butylene)-polystyrene triblock copolymersavailable from Asahi Kasei Elastomer as TUFTEC™ P1000 and P2000; thepolystyrene-poly(ethylene-butylene)-polystyrene triblock copolymercomprising 60 weight polystyrene available from Kuraray as SEPTON™S8104; the polystyrene-poly(ethylene-ethylene/propylene)-polystyrenetriblock copolymers available from Kuraray as SEPTON™ S4044, S4055,S4077, and S4099; and thepolystyrene-poly(ethylene-propylene)-polystyrene triblock copolymercomprising 65 weight percent polystyrene available from Kuraray asSEPTON™ S2104.

In some embodiments, the impact modifier is apolystyrene-poly(ethylene-butylene)-polystyrene triblock copolymerhaving a polystyrene content of 25 to 35 weight percent and a weightaverage molecular weight of 200,000 to 400,000 atomic mass units.

When present, the impact modifier can be used in an amount of 1 to 10weight percent, specifically 1 to 5 weight percent, based on the totalweight of the composition.

The composition can, optionally, further comprise a hydrocarbon resin.Examples of hydrocarbon resins are aliphatic hydrocarbon resins,hydrogenated aliphatic hydrocarbon resins, aliphatic/aromatichydrocarbon resins, hydrogenated aliphatic/aromatic hydrocarbon resins,cycloaliphatic hydrocarbon resins, hydrogenated cycloaliphatic resins,cycloaliphatic/aromatic hydrocarbon resins, hydrogenatedcycloaliphatic/aromatic hydrocarbon resins, hydrogenated aromatichydrocarbon resins, terpene resins, hydrogenated terpene resins,terpene-phenol resins, rosins, and rosin esters, hydrogenated rosins androsin esters, and mixtures thereof. As used herein, “hydrogenated”, whenreferring to the hydrocarbon resin, includes fully, substantially, andpartially hydrogenated resins. Suitable aromatic resins include aromaticmodified aliphatic resins, aromatic modified cycloaliphatic resins, andhydrogenated aromatic hydrocarbon resins having an aromatic content of 1to 30 weight percent. Any of the above resins can be grafted with anunsaturated ester or anhydride using methods known in the art. Suchgrafting can provide enhanced properties to the resin. In someembodiments, the hydrocarbon resin is a hydrogenated aromatichydrocarbon resin.

Suitable hydrocarbon resins are commercially available and include, forexample, EMPR™ 100, 101, 102, 103, 104, 105, 106, 107, 108, 109, 110,116, 117, and 118 resins, and OPPERA™ resins, available from ExxonMobilChemical Company; ARKON™ P140, P125, P115, M115, and M135, and SUPERESTER™ rosin esters available from Arakawa Chemical Company of Japan;SYLVARES™ polyterpene resins, styrenated terpene resins and terpenephenolic resins available from Arizona Chemical Company; SYLVATAC™ andSYLVALITE™ rosin esters available from Arizona Chemical Company;NORSOLENE™ aliphatic aromatic resins available from Cray Valley;DERTOPHENE™ terpene phenolic resins and DERCOLYTE™ polyterpene resinsavailable from DRT Chemical Company; EASTOTAC™ resins, PICCOTAC™ resins,REGALITE™ and REGALREZ™ hydrogenated cycloaliphatic/aromatic resins, andPICCOLYTE™ and PERMALYN™ polyterpene resins, rosins, and rosin estersavailable from Eastman Chemical Company; WINGTACK™ resins available fromGoodyear Chemical Company; coumarone/indene resins available fromNeville Chemical Company; QUINTONE™ acid modified C5 resins, C5/C9resins, and acid-modified C5/C9 resins available from Nippon Zeon; andCLEARON™ hydrogenated terpene resins available from Yasuhara. In someembodiments, the hydrocarbon resin is a hydrogenated terpene resin. Insome embodiments, the hydrocarbon resin is a saturated polyalicyclichydrocarbon resin.

The hydrocarbon resin can have a softening point of at least 120° C.measured according to ASTM E28. Specifically, the softening point can be120 to 180° C., specifically 130 to 170° C., more specifically 140 to160° C. In some embodiments, the hydrocarbon resin comprises ahydrogenated alicyclic hydrocarbon resin, a hydrogenated terpene resin,or a combination thereof. In some embodiments, the hydrocarbon resincomprises a hydrogenated alicyclic hydrocarbon resin having a softeningpoint of 120 to 135° C. An example of such a resin is ARKON™ P125 havinga softening point of about 125° C., available from Arakawa ChemicalCompany, In some embodiments, the hydrocarbon resin comprises ahydrogenated alicyclic hydrocarbon resin having a softening point of 135to 145° C. An example of such a resin is ARKON™ P140 having a softeningpoint of about 140° C., available from Arakawa Chemical Company, In someembodiments, the hydrocarbon resin comprises a hydrogenated terpeneresin having a softening point of 145 to 160° C. An example of such aresin is CLEARON™ P150 available from Yasuhara.

When present, the hydrocarbon resin can be used in an amount of 1 to 8weight percent, specifically 2 to 6 weight percent, based on the totalweight of the composition.

The composition can, optionally, further comprise a trihydrocarbylphosphite. Trihydrocarbyl phosphites have the general structureP(OR³⁰)₃, wherein each occurrence of R³⁰ is independently C₁-C₁₈hydrocarbyl. In some embodiments, each R³⁰ is independently C₆-C₁₈alkyl. In other embodiments, at least one R³⁰ is C₆-C₁₈ aryl. In someembodiments, each occurrence of R¹⁹ is independently an unsubstituted orsubstituted C₆-C₁₈ aryl. Suitable trihydrocarbyl phosphites include, forexample, trioctyl phosphite, tridecyl phosphite, tridodecyl phosphite,phenyl didecyl phosphite, decyl diphenyl phosphite, triphenyl phosphite,tritolyl phosphites, tris(2,4-di-tert-butylphenyl)phosphite,bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, and the like,and combinations thereof. Suitable trihydrocarbyl phosphites furtherinclude spiro diphosphites such as, for example,3,9-bis[2,4-bis(1,1-dimethylethyl)phenoxy]-2,4,8,10-tetraoxa-3,9-diphosphaspiro[5.5]undecane(CAS Reg. No. 26741-53-7; commercially available from Ciba under thetrade name IRGAFOS™ 126). In some embodiments, the aryl phosphitecomprises tris(2,4-di-tert-butylphenyl)phosphite (CAS Reg. No.31570-04-4). In some embodiments, the aryl phosphite comprisesbis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite (CAS Reg. No.26741-53-7).

When present, the trihydrocarbyl phosphite can be used in an amount of0.05 to 1 weight percent, specifically 0.1 to 0.5 weight percent, basedon the total weight of the composition.

The composition can, optionally, further comprise linear low densitypolyethylene (LLDPE). Linear low density polyethylene is a copolymer ofethylene and a longer chain olefin such as 1-butene, 1-hexene, or1-octene. In some embodiments, the linear low density polyethylene is acopolymer of ethylene and 1-butene. Linear low density polyethylenetypically has a density of about 0.92 grams/centimeter³. When present,the linear low density polyethylene can be used in an amount of 0.5 to 5weight percent, specifically 0.5 to 3 weight percent, based on the totalweight of the composition.

The composition can, optionally, further comprise one or more additivesknown in the thermoplastics art. For example, the composition can,optionally, further comprise an additive chosen from stabilizers, moldrelease agents, lubricants, processing aids, drip retardants, nucleatingagents, UV blockers, dyes, pigments, antioxidants, anti-static agents,blowing agents, mineral oil, metal deactivators, antiblocking agents,and the like, and combinations thereof. When present, such additives aretypically used in a total amount of less than or equal to 5 weightpercent, specifically less than or equal to 4 weight percent, morespecifically less than or equal to 3 weight percent, based on the totalweight of the composition.

The composition can, optionally, exclude polymers other than thoserequired. For example, the composition can comprise less than or equalto 1 weight percent of each of polyamides and polyesters. In someembodiments, the composition comprises less than or equal to 4 weightpercent, specifically less than or equal to 3 weight percent, morespecifically less than or equal to 2 weight percent, of polyolefins. Insome embodiments, the composition comprises less than or equal to 1weight percent of polyolefins other than linear low densitypolyethylene. In other embodiments, the composition comprises less thanor equal to 1 weight percent of any polyolefins.

One advantage of the composition is that it can achieve a UL 94 V-0rating without using the halogenated flame retardants that are typicallyemployed in glass-filled polyester compositions utilized for similarproduct applications. Thus, the composition can comprise less than orequal to 0.1 weight percent halogens, specifically less than or equal to0.01 weight percent halogens, based on the total weight of thecomposition. In some embodiments, composition is halogen-free.

In some embodiments, the article is a fuser holder, and the compositioncomprises 2 to 10 weight percent of a poly(phenylene ether)-polysiloxaneblock copolymer reaction product, and further comprises 55 to 75 weightpercent of a second poly(phenylene ether). In these embodiments, thereinforcing filler amount is, optionally, 10 to 20 weight percent, andthe reinforcing filler optionally comprises glass fibers. Also in theseembodiments, the composition optionally further comprises 1 to 5 weightpercent of a hydrogenated block copolymer of an alkenyl aromaticcompound and a conjugated diene.

In a very specific embodiment, the article is a fuser holder, thepoly(phenylene ether)-polysiloxane copolymer comprises a poly(phenyleneether)-polysiloxane block copolymer provided in the form of apoly(phenylene ether)-polysiloxane block copolymer reaction product, thepoly(phenylene ether)-polysiloxane block copolymer comprises apoly(phenylene ether) block comprising phenylene ether repeat unitshaving the structure

anda polysiloxane block having the structure

wherein n is 30 to 60; the reinforcing filler comprises glass fibers;the flame retardant comprises bisphenol A bis(diphenyl phosphate); thecomposition comprises 2 to 10 weight percent of the poly(phenyleneether)-polysiloxane block copolymer reaction product, 5 to 15 weightpercent of the flame retardant, and 10 to 20 weight percent of thereinforcing filler; and the composition further comprises 55 to 75weight percent of a second poly(phenylene ether) comprisingpoly(2,6-dimethyl-1,4-phenylene ether), and 1 to 5 weight percent of apolystyrene-poly(ethylene-butylene)-polystyrene block copolymer.

In some embodiments, the article is selected from the group consistingof fan blades, battery parts for hybrid and electric vehicles, parts forautomotive kinetic energy recovery systems, and electric vehiclejunction boxes, and the composition comprises 53 to 63 weight percent ofa poly(phenylene ether)-polysiloxane block copolymer reaction product.In these embodiments, the reinforcing filler amount is, optionally, 15to 25 weight percent, and the reinforcing filler optionally comprisesglass fibers. Also in these embodiments, the composition optionallycomprises 0 to 4 weight percent of a hydrogenated block copolymer of analkenyl aromatic compound and a conjugated diene. Also in theseembodiments, the composition optionally comprises 0.5 to 3 weightpercent of a linear low density polyethylene.

In a very specific embodiment, the article is selected from the groupconsisting of fan blades, battery parts for hybrid and electricvehicles, parts for automotive kinetic energy recovery systems, andelectric vehicle junction boxes; the poly(phenylene ether)-polysiloxanecopolymer comprises a poly(phenylene ether)-polysiloxane block copolymerprovided in the form of a poly(phenylene ether)-polysiloxane blockcopolymer reaction product; the poly(phenylene ether)-polysiloxane blockcopolymer comprises a poly(phenylene ether) block comprising phenyleneether repeat units having the structure

anda polysiloxane block having the structure

wherein n is 30 to 60; the reinforcing filler comprises glass fibers;the flame retardant comprises bisphenol A bis(diphenyl phosphate); thecomposition comprises 53 to 63 weight percent of the poly(phenyleneether)-polysiloxane block copolymer reaction product, 15 to 25 weightpercent of the flame retardant, and 15 to 25 weight percent of thereinforcing filler; and the composition further comprises 0.5 to 3weight percent of a linear low density polyethylene.

As described above, the article can be a fuser holder for anelectrophotographic copier, a fan blade, a battery part for hybrid andelectric vehicles, a part for an automotive kinetic energy recoverysystem, or an electric vehicle junction box. Other than their beingfabricated with the composition described herein, such articles areknown, as are methods for their fabrication. For example, U.S. Pat. No.5,499,087 of Hiraoka et al. describes a fuser holder for anelectrophotographic copier. Suitable methods of forming such articlesinclude single layer and multilayer sheet extrusion, injection molding,blow molding, film extrusion, profile extrusion, pultrusion, compressionmolding, thermoforming, pressure forming, hydroforming, vacuum forming,and the like. Combinations of the foregoing article fabrication methodscan be used. In some embodiments, the article is formed by injectionmolding. In some of these embodiments, the injection molding uses abarrel temperature of 285 to 330° C., specifically 295 to 325° C., and amold temperature of 60 to 120° C., specifically 80 to 110° C.

All ranges disclosed herein are inclusive of the endpoints, and theendpoints are independently combinable with each other. Each rangedisclosed herein constitutes a disclosure of any point or sub-rangelying within the disclosed range.

The invention includes at least the following embodiments.

Embodiment 1

An article comprising a composition, wherein the article is selectedfrom the group consisting of fuser holders for electrophotographiccopiers, fan blades, battery parts for hybrid and electric vehicles,parts for automotive kinetic energy recovery systems, and electricvehicle junction boxes; wherein the composition comprises 0.5 to 85weight percent of a poly(phenylene ether)-polysiloxane copolymercomprising a poly(phenylene ether)-polysiloxane block copolymer, apoly(phenylene ether)-polysiloxane graft copolymer, or a combinationthereof; 5 to 25 weight percent of a flame retardant comprising anorganophosphate ester, a phosphazene, or a combination thereof; and 10to 35 weight percent of a reinforcing filler; wherein all weight percentvalues are based on the total weight of the composition; provided thatwhen the article is a fuser holder, the composition comprises 2 to 10weight percent of a poly(phenylene ether)-polysiloxane block copolymerreaction product comprising the a poly(phenylene ether)-polysiloxaneblock copolymer and a first a poly(phenylene ether), and furthercomprises 55 to 75 weight percent of a second poly(phenylene ether).

Embodiment 2

The article of embodiment 1, wherein the poly(phenyleneether)-polysiloxane copolymer comprises the poly(phenyleneether)-polysiloxane block copolymer.

Embodiment 3

The article of embodiment 2, wherein composition comprises apoly(phenylene ether)-polysiloxane block copolymer reaction productcomprising the poly(phenylene ether)-polysiloxane block copolymer and afirst poly(phenylene ether), and wherein the poly(phenyleneether)-polysiloxane block copolymer comprises a poly(phenylene ether)block comprising phenylene ether repeat units having the structure

anda polysiloxane block having the structure

wherein n is 30 to 60.

Embodiment 4

The article of embodiment 2, wherein the poly(phenyleneether)-polysiloxane block copolymer comprises a poly(phenyleneether)-polysiloxane multiblock copolymer.

Embodiment 5

The article of embodiment 1, wherein the poly(phenyleneether)-polysiloxane copolymer comprises the poly(phenyleneether)-polysiloxane graft copolymer.

Embodiment 6

The article of any of embodiments 1-5, wherein the reinforcing filler isselected from the group consisting of glass fibers, carbon fibers,wollastonite, halloysite, clays, talcs, micas, glass flakes, solid glassbeads, hollow glass beads, solid ceramic beads, hollow ceramic beads,and combinations thereof.

Embodiment 7

The article of any of embodiments 1-5, wherein the reinforcing fillercomprises glass fibers.

Embodiment 8

The article of any of embodiments 1-7, wherein the flame retardantcomprises the organophosphate ester.

Embodiment 9

The article of embodiment 8, wherein the organophosphate ester comprisesbisphenol A bis(diphenyl phosphate).

Embodiment 10

The article of any of embodiments 1-9, wherein the flame retardantcomprises the phosphazene.

Embodiment 11

The article of embodiment 10, wherein the flame retardant comprises acyclic oligo(bis(phenoxy)phosphazene), a linearoligo(bis(phenoxy)phosphazene), a linear poly(bis(phenoxy)phosphazene),a crosslinked poly(bis(phenoxy)phosphazene), or a combination thereof.

Embodiment 12

The article of any of embodiments 1-11, wherein the composition furthercomprises 1 to 10 weight percent of an impact modifier selected from thegroup consisting of rubber-modified polystyrenes, unhydrogenated blockcopolymers of an alkenyl aromatic monomer and a conjugated diene,hydrogenated block copolymers of an alkenyl aromatic monomer and aconjugated diene, acrylate core-shell impact modifiers, and combinationsthereof.

Embodiment 13

The article of embodiment 1, wherein the article is a fuser holder; andwherein the composition comprises 2 to 10 weight percent of apoly(phenylene ether)-polysiloxane block copolymer reaction productcomprising the poly(phenylene ether)-polysiloxane block copolymer and afirst poly(phenylene ether); and wherein the composition furthercomprises 55 to 75 weight percent of a second poly(phenylene ether).

Embodiment 14

The article of embodiment 13, wherein the composition comprises 10 to 20weight percent of the reinforcing filler, and the reinforcing fillercomprises glass fibers.

Embodiment 15

The article of embodiment 13 or 14, wherein the composition furthercomprises 1 to 5 weight percent of a hydrogenated block copolymer of analkenyl aromatic compound and a conjugated diene.

Embodiment 16

The article of embodiment 1, wherein the article is a fuser holder;wherein the composition comprises a poly(phenylene ether)-polysiloxaneblock copolymer reaction product comprising the poly(phenyleneether)-polysiloxane block copolymer and a first poly(phenylene ether);wherein the poly(phenylene ether)-polysiloxane block copolymer comprisesa poly(phenylene ether) block comprising phenylene ether repeat unitshaving the structure

anda polysiloxane block having the structure

wherein n is 30 to 60; wherein the first poly(phenylene ether) comprisespoly(2,6-dimethyl-1,4-phenylene ether); wherein the reinforcing fillercomprises glass fibers; wherein the flame retardant comprises bisphenolA bis(diphenyl phosphate); wherein the composition comprises 2 to 10weight percent of the poly(phenylene ether)-polysiloxane block copolymerreaction product, 5 to 15 weight percent of the flame retardant, and 10to 20 weight percent of the reinforcing filler; and wherein thecomposition further comprises 55 to 75 weight percent of a secondpoly(phenylene ether) comprising poly(2,6-dimethyl-1,4-phenylene ether),and 1 to 5 weight percent of apolystyrene-poly(ethylene-butylene)-polystyrene block copolymer.

Embodiment 17

The article of embodiment 1, wherein the article is selected from thegroup consisting of fan blades, battery parts for hybrid and electricvehicles, parts for automotive kinetic energy recovery systems, andelectric vehicle junction boxes; and wherein the composition comprises53 to 63 weight percent of a poly(phenylene ether)-polysiloxane blockcopolymer reaction product comprising the poly(phenyleneether)-polysiloxane block copolymer and a first poly(phenylene ether).

Embodiment 18

The article of embodiment 17, wherein the composition comprises 15 to 25weight percent of the reinforcing filler, and the reinforcing fillercomprises glass fibers.

Embodiment 19

The article of embodiment 17 or 18, wherein the composition comprises 0to 4 weight percent of a hydrogenated block copolymer of an alkenylaromatic compound and a conjugated diene.

Embodiment 20

The article of any of embodiments 17-19, wherein the composition furthercomprises 0.5 to 3 weight percent of a linear low density polyethylene.

Embodiment 21

The article of embodiment 1, wherein the article is selected from thegroup consisting of fan blades, battery parts for hybrid and electricvehicles, parts for automotive kinetic energy recovery systems, andelectric vehicle junction boxes; wherein the composition comprises apoly(phenylene ether)-polysiloxane block copolymer reaction productcomprising the poly(phenylene ether)-polysiloxane block copolymer and afirst poly(phenylene ether); wherein the poly(phenyleneether)-polysiloxane block copolymer comprises a poly(phenylene ether)block comprising phenylene ether repeat units having the structure

anda polysiloxane block having the structure

wherein n is 30 to 60; wherein the reinforcing filler comprises glassfibers; wherein the flame retardant comprises bisphenol A bis(diphenylphosphate); wherein the composition comprises 53 to 63 weight percent ofthe poly(phenylene ether)-polysiloxane block copolymer reaction product,15 to 25 weight percent of the flame retardant, and 15 to 25 weightpercent of the reinforcing filler; and wherein the composition furthercomprises 0.5 to 3 weight percent of a linear low density polyethylene.

The invention is further illustrated by the following non-limitingexamples.

Comparative Examples 1-15

These comparative examples utilize poly(phenylene ether) homopolymer,rather than poly(phenylene ether)-polysiloxane block copolymer reactionproduct. Components used to prepare the compositions are summarized inTable 1.

TABLE 1 Component Description PPE 0.46 Poly(2,6-dimethyl-1,4-phenyleneether), CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about0.46 deciliter per gram measured in chloroform at 25° C.; available asPPO ™ from SABIC Innovative Plastics. PPE 0.40Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No. 25134-01-4, havingan intrinsic viscosity of about 0.40 deciliter per gram measured inchloroform at 25° C.; available as PPO ™ 640 from SABIC InnovativePlastics. PPE 0.33 Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No.25134-01-4, having an intrinsic viscosity of about 0.33 deciliter pergram measured in chloroform at 25° C.; available as PPO ™ 630 from SABICInnovative Plastics. PPE 0.30 Poly(2,6-dimethyl-1,4-phenylene ether),CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about 0.30deciliter per gram measured in chloroform at 25° C.; available as PPO ™808 from SABIC Innovative Plastics. PPE-Si A mixture ofpoly(2,6-dimethyl-1,4-phenylene ether) (CAS Reg. No. 24938-67-8) andpoly(2,6-dimethyl-1,4-phenylene ether)-polydimethylsiloxane blockcopolymer (CAS Reg. No. 1202019-56-4), the mixture having a polysiloxanecontent of about 5 weight percent and an intrinsic viscosity of about0.4 deciliter per gram as measured in chloroform at 25° C.; preparedaccording to the procedure of U.S. Pat. No. 8,017,697 to Carrillo etal., Example 16. SEBS Polystyrene-poly(ethylene/butylene)-polystyrenetriblock copolymer, CAS Reg. No. 66070-58-4, having a polystyrenecontent of 30-33 weight percent and a weight average molecular weight of240,000-301,000 atomic mass units; obtained as KRATON ™ G1651 fromKraton Performance Polymers Inc. AO 168 Tris(2,4-di-tert-butylphenyl)phosphite, CAS Reg. No. 31570-04-4, available from BASF Corp. asIRGAFOS ™ 168, or from Chemtura as ALKANOX ™ 240. AO 626Bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, CAS Reg. No.26741- 53-7, available from Chemtura as ULTRANOX ™ 626 HCR Saturatedpolyalicyclic hydrocarbon resin, CAS Reg. No. 4742-16-1, available fromArakawa Chemical as ARKON ™ P-125. HIPS Rubber-modified polystyrene, CASReg. No. 9003-55-8, available from SABIC Innovative Plastics asHIPS3190. Clay Water-washed kaolin clay, CAS Reg. No. 1332-58-7,available as KaMin POLYFIL ™ HG90 from KaMin Performance Minerals. MicaPhlogopite mica, CAS Reg. No. 12001-26-2, available from ImerysPerformance Minerals as SUZORITE ™ HK-200. Glass Fiber Chopped glassfiber having a diameter of about 14 micrometers and a pre- compoundedlength of about 4 millimeters; available from Owens Corning as 122Y-14C.Carbon Black Carbon black pigment, CAS Reg. No. 1333-86-4, availablefrom Cabot as BLACK PEARLS ™ 800 or MONARCH ™ 800. LLDPE Linear lowdensity polyethylene (copolymer of ethylene and 1-butene), CAS Reg. No.25087-34-7, having a density of 0.925 grams per cubic centimeter and amelt volume flow rate of 20 cubic centimeters per 10 minutes at 190° C.and 2.16 kilogram load, available from ExxonMobil as ESCORENE ™LL5100.09. MgO Magnesium oxide, CAS Reg. No. 1309-48-4, available fromKyowa Chemical Co. Ltd. as KYOWAMAG ™ 150. ZnS Zinc sulfide, CAS Reg.No. 1314-98-3, available from Sachtleben Chemie GmbH as SACHTOLITH ™HD-S. But-TPP t-Butylated triphenyl phosphate, CAS Reg. No. 220352-35-2,available as PHOSFLEX ™ 71B from Supresta LLC. BPADP Bisphenol Abis(diphenyl phosphate), CAS Reg. No. 181028-79-5; obtained asFYROFLEX ™ BDP from Supresta LLC, or REOFOS ™ BAPP from Great LakesChemical Co. Ltd.

Resin compositions were compounded on a 30 millimeter Werner &Pfleiderer ZSK twin-screw extruder operating at 350 rotations per minuteand a throughput of 18 kilograms per hour (40 pounds per hour) and usingbarrel set temperatures of 240° C./260° C./290° C./290° C./290° C. fromthe feed port to die. Glass fibers were added downstream to theextruder, while all other solid components were added at the feed throatand the liquid flame retardant (But-TPP or BPADP) was injected at a portbetween the feed throat and the glass fiber feed location. Thecompounded resins were pelletized by strand-cutting.

Test articles for ASTM determinations of heat deflection temperature andflexural properties were injection molded on a 120 Ton VanDorn injectionmolding machine using a barrel temperature of 288-310° C. (550-590° F.)and a mold temperature of about 88° C. (about 190° F.). Flame bars with1.0 or 1.5 millimeter thickness were injection molded on an 80 TonVanDorn injection molding machine using a barrel temperature of 299-321°C. (570-610° F.) and a mold temperature of 88-99° C. (190-210° F.).

Flame retardancy of injection molded flame bars was determined accordingto Underwriter's Laboratory Bulletin 94 “Tests for Flammability ofPlastic Materials, UL 94”, 20 mm Vertical Burning Flame Test. Beforetesting, flame bars with a thickness of 1.0 or 1.5 millimeters wereconditioned at 23° C. and 50% relative humidity for at least 24 hours.In the UL 94 20 mm Vertical Burning Flame Test, a set of ten flame barswas tested. For each bar, a flame was applied to the bar then removed,and the time required for the bar to self-extinguish (first afterflametime, t1) was noted. The flame was then reapplied and removed, and thetime required for the bar to self-extinguish (second afterflame time,t2) and the post-flame glowing time (afterglow time, t3) were noted. Toachieve a rating of V-0, the afterflame times t1 and t2 for eachindividual specimen must have been less than or equal to 10 seconds; andthe total afterflame time for all ten specimens (t1 plus t2 for all tenspecimens) must have been less than or equal to 100 seconds; and thesecond afterflame time plus the afterglow time for each individualspecimen (t2+t3) must have been less than or equal to 30 seconds; and nospecimen can have flamed or glowed up to the holding clamp; and thecotton indicator cannot have been ignited by flaming particles or drops.To achieve a rating of V-1, the afterflame times t1 and t2 for eachindividual specimen must have been less than or equal to 30 seconds; andthe total afterflame time for all ten specimens (t1 plus t2 for all tenspecimens) must have been less than or equal to 500 seconds; and thesecond afterflame time plus the afterglow time for each individualspecimen (t2+t3) must have been less than or equal to 60 seconds; and nospecimen can have flamed or glowed up to the holding clamp; and thecotton indicator cannot have been ignited by flaming particles or drops.To achieve a rating of V-2, the afterflame times t1 and t2 for eachindividual specimen must have been less than or equal to 30 seconds; andthe total afterflame time for all ten specimens (t1 plus t2 for all tenspecimens) must have been less than or equal to 250 seconds; and thesecond afterflame time plus the afterglow time for each individualspecimen (t2+t3) must have been less than or equal to 60 seconds; and nospecimen can have flamed or glowed up to the holding clamp; but thecotton indicator can have been ignited by flaming particles or drops.Compositions not achieving a rating of V-2 were considered to havefailed.

Heat deflection temperature (HDT) values, expressed in units of degreescentigrade, were determined according to ASTM D 648-07 using 6.4millimeter thick bars (except where specified as 3.2 millimeterthickness), an edgewise test direction, a support span of 100millimeters (Method B), a stress of 1.82 megapascals, a deflection of0.25 millimeters at reading, a heating rate of 2° C./minute, and threespecimens per composition.

Flexural modulus and flexural strength values, each in units ofmegapascals, were determined at 23° C. according to ASTM D 790-07e1using 6.4 millimeter thick bars, a support span of 101.6 millimeters, atest speed of 2.54 millimeters/minute (0.1 inch/minute; Procedure A),and three specimens per composition.

Compositions and results are summarized in Table 2, where componentamounts are expressed in weight percent based on the total weight of thecomposition.

The Table 2 results show that the achievement of a flame retardancyrating of V-0 at a bar thickness of 1.5 millimeters is limited toComparative Examples 1-3 with very high flame retardant concentrations(≧21.00 weight percent) and correspondingly low heat deflectiontemperatures (≦112° C.). A flame retardancy rating of V-0 at 1.0millimeter thickness was only observed for Comparative Example 1 with alow heat deflection temperature of 106° C.

TABLE 2 C. Ex. 1 C. Ex. 2 C. Ex. 3 C. Ex. 4 C. Ex. 5 COMPOSITIONS PPE0.40 63 56 49 67.5 60 BPADP 27 24 21 22.5 20 Glass fiber 10 20 30 10 20PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 Fail Fail UL 94 rating at1.0 mm V-0 V-1 V-1 V-1 V-1 HDT (° C.) 106 111 112 120 124 Flex. modulus(MPa) 4670 7120 9610 4670 6850 Flex. strength (MPa) 144 153 159 145 149C. Ex. 6 C. Ex. 7 C. Ex. 8 C. Ex. 9 C. Ex. 10 COMPOSITIONS PPE 0.40 52.572 64 56 76.5 BPADP 17.5 18 16 14 13.5 Glass fiber 30 10 20 30 10PROPERTIES UL 94 rating at 1.5 mm V-1 V-1 V-1 V-1 V-1 UL 94 rating at1.0 mm V-1 V-1 V-1 V-1 V-1 HDT (° C.) 124 133 137 138 149 Flex. modulus(MPa) 9090 4370 6490 8380 4250 Flex. strength (MPa) 158 147 149 151 145C. Ex. 11 C. Ex. 12 C. Ex. 13 C. Ex. 14 C. Ex. 15 COMPOSITIONS PPE 0.4068 59.5 81 72 63 BPADP 12 10.5 9 8 7 Glass fiber 20 30 10 20 30PROPERTIES UL 94 rating at 1.5 mm Fail V-1 V-1 V-1 V-1 UL 94 rating at1.0 mm V-1 Fail V-1 V-1 V-1 HDT (° C.) 152 154 164 168 170 Flex. modulus(MPa) 6000 8050 4100 5830 7890 Flex. strength (MPa) 142 152 142 145 155

Comparative Examples 16-23

Eight comparative examples were prepared using poly(phenylene ether)homopolymer and the hydrogenated block copolymer SEBS. These examplesillustrate that it is not feasible to achieve a V-0 rating at 1.5millimeter thickness in a composition with a heat deflection temperatureof at least 150° C. and at least 10% glass fiber reinforcement, eventhough the corresponding unfilled compositions (Comparative Examples 16and 20) have a V-0 flame retardancy. Relative to the property balanceexhibited by the inventive composition, unfilled Comparative Examples 16and 20 are deficient, at least, in flexural modulus, and filledComparative Examples 17-19 and 21-23 are deficient, at least, in UL 94rating.

TABLE 3 C. Ex. 16 C. Ex. 17 C. Ex. 18 C. Ex. 19 C. Ex. 20 COMPOSITIONSPPE 0.46 84.70 76.23 67.76 72.00 82.70 BPADP 10.00 9.00 8.00 8.50 12.00SEBS 5.00 4.5 4.00 4.25 5.00 AO 168 0.30 0.27 0.24 0.25 0.30 Glass fiber0.00 10 20 10.00 0.00 Clay 0.00 0.00 0.00 5.00 0.00 PROPERTIES UL 94rating at 1.5 mm V-0 V-1 V-1 V-1 V-0 HDT (° C.) 146 159 163 159 139Flex. modulus (MPa) 2520 3721 5234 4235 2570 Flex. strength (MPa) 106122 132 136 108 C. Ex. 21 C. Ex. 22 C. Ex. 23 COMPOSITIONS PPE 0.4674.43 66.16 70.30 BPADP 10.80 9.60 10.20 SEBS 4.50 4.00 4.25 AO 168 0.270.24 0.25 Glass fiber 10.00 20.00 10.00 Clay 0.00 0.00 5.00 PROPERTIESUL 94 rating at 1.5 mm V-1 V-1 V-1 HDT (° C.) 152 156 153 Flex. modulus(MPa) 3937 5363 4297 Flex. strength (MPa) 128 131 135

Examples 1-6, Comparative Examples 24 and 25

These inventive and comparative examples illustrate the use of apoly(phenylene ether)-polysiloxane block copolymer in combination withthe hydrogenated block copolymer SEBS. Inventive Examples 1-6 all haveheat deflection temperature values of at least 155° C., as well as UL 94ratings of V-0 at 1.5 millimeter thickness, and flexural modulus valuesgreater than 3,500 megapascals. Comparative Examples 24 and 25 areunfilled and exhibit substantially lower heat deflection temperaturevalues, flexural modulus values, and flexural strength values.

TABLE 4 C. Ex. 24 Ex. 1 Ex. 2 Ex. 3 C. Ex. 25 COMPOSITIONS PPE-Si 87.7078.93 70.16 74.55 85.70 BPADP 7.00 6.30 5.60 5.95 9.00 SEBS 5.00 4.504.00 4.25 5.00 AO 168 0.30 0.27 0.24 0.25 0.30 Glass fiber 0.00 10.0020.00 10.00 0.00 Clay 0.00 0.00 0.00 5.00 0.00 PROPERTIES UL 94 ratingat V-0 V-0 V-0 V-0 V-0 1.5 mm HDT (° C.) 149 163 168 163 140 Flex.modulus 2310 3506 4942 3891 2350 (MPa) Flex. strength (MPa) 94 119 133125 96 Ex. 4 Ex. 5 Ex. 6 COMPOSITIONS PPE-Si 77.13 68.56 72.85 BPADP8.10 7.20 7.65 SEBS 4.50 4.00 4.25 AO 168 0.27 0.24 0.25 Glass fiber10.00 20.00 10.00 Clay 0.00 0.00 5.00 PROPERTIES UL 94 rating at 1.5 mmV-0 V-0 V-0 HDT (° C.) 155 160 158 Flex. modulus (MPa) 3739 5027 4039Flex. strength (MPa) 123 130 129

Examples 7-15, Comparative Example 26

These inventive and comparative examples illustrate means of achievingimproved melt flow.

Melt volume flow rate (MVR) values, expressed in units of cubiccentimeters per 10 minutes, were determined according to ASTM D 1238-04at 300° C. using a load of 5 kilograms, automatic timing (Procedure B),a capillary diameter of 2.0955 millimeters, a capillary length of 8.00millimeters, a test specimen form of pellets, specimen conditioning forone hour at 70° C. prior to testing, and one sample with five readingsper composition.

The results in Table 5 show that the inventive compositions can bemodified to increase melt flow while still maintaining a high heatdeflection temperature and a UL 94 rating of V-0 at 1.5 millimeters.Inventive Example 13 shows that a reduced concentration ofpoly(phenylene ether)-polysiloxane block copolymer also still results inV-0 at 1.5 mm. Inventive Example 15 illustrates the use of a mixedfiller reinforcement. The examples also show that melt flow increasescan be accomplished through use of a hydrocarbon resin flow promoter(Examples 10-15) and/or a phosphite antioxidant like AO 626. InventiveExample 7, without either hydrocarbon resin or phosphite antioxidant,exhibits relatively lower melt flow. Comparative Example 26 shows againthat with poly(phenylene ether) homopolymer rather than poly(phenyleneether)-polysiloxane block copolymer reaction product, even a higherconcentration of flame retardant does not result in V-0 flammabilityrating at 1.5 millimeters.

TABLE 5 Ex. 7 Ex. 8 Ex. 9 Ex. 10 Ex. 11 COMPOSITIONS PPE-Si 68.66 68.2667.86 68.26 68.26 PPE 0.40 0.00 0.00 0.00 0.00 0.00 BPADP 6.97 6.97 6.976.97 6.97 SEBS 3.98 3.98 3.98 1.99 0.00 HCR 0.00 0.00 0.00 1.99 3.98 AO626 0.00 0.40 0.80 0.40 0.40 Carbon black 0.50 0.50 0.50 0.50 0.50 Glassfiber 19.90 19.90 19.90 19.90 19.90 Mica 0.00 0.00 0.00 0.00 0.00PROPERTIES UL 94 rating at V-0 V-0 V-0 V-0 V-0 1.5 mm HDT (° C.) 161 158157 156 153 MVR (cc/10 min) 2.8 8.8 12.6 11.6 14.1 Flex. modulus (MPa)5150 5180 5310 5320 5500 Flex. strength (MPa) 137 136 131 131 138 Ex. 12Ex. 13 Ex. 14 Ex. 15 C. Ex. 26 COMPOSITIONS PPE-Si 67.86 33.43 77.2172.74 0.00 PPE 0.40 0.00 33.43 0.00 0.00 65.27 BPADP 6.97 8.36 7.96 7.469.95 SEBS 0.00 1.99 1.99 1.99 3.98 HCR 3.98 1.99 1.99 1.99 0.00 AO 6260.80 0.40 0.40 0.40 0.40 Carbon black 0.50 0.50 0.50 0.50 0.50 Glassfiber 19.90 19.90 9.95 9.95 19.90 Mica 0.00 0.00 0.00 4.98 0.00PROPERTIES UL 94 rating at V-0 V-0 V-0 V-0 V-1 1.5 mm HDT (° C.) 151 153152 153 155 MVR (cc/10 min) 21.8 13.1 16.3 13.4 8.28 Flex. modulus (MPa)5660 5480 3910 4367 5640 Flex. strength (MPa) 134 133 122 124 136

Examples 16-19

These inventive examples illustrate that omission of hydrogenated blockcopolymer is associated with even higher heat deflection temperaturevalues.

TABLE 6 Ex. 16 Ex. 17 Ex. 18 Ex. 19 COMPOSITIONS PPE-Si 76.32 71.8467.86 73.83 BPADP 7.46 6.97 6.97 4.98 HCR 0.00 0.00 3.98 0.00 AO 6260.80 0.80 0.80 0.80 Carbon black 0.50 0.50 0.50 0.50 Glass fiber 9.9519.90 19.90 19.90 Mica 4.98 0.00 0.00 0.00 PROPERTIES UL 94 rating at1.5 mm V-0 V-0 V-0 V-0 HDT (° C.) 157 159 153 168 MVR (cc/10 min) 18 1423 9 Flex. modulus (MPa) 4700 5680 5650 5520 Flex. strength (MPa) 118136 128 135

Examples 20 and 21, Comparative Examples 27 and 28

These inventive and comparative examples, all with 20% glass fiberreinforcement, illustrate that the improved flame retardancy associatedwith the use of poly(phenylene ether)-polysiloxane block copolymerreaction product rather than poly(phenylene ether) homopolymer can beobtained without sacrificing heat resistance. Comparative Example 28also illustrates that a reduction of HIPS concentration and increases inflame retardant and poly(phenylene ether) homopolymer, all relative toComparative Example 27, are not sufficient to result in V-0 flameperformance at 1.5 millimeters.

TABLE 7 C. Ex. 27 Ex. 20 C. Ex. 28 Ex. 21 COMPOSITIONS TPPE 0.46 48.000.00 55.00 0.00 PPE-Si 0.00 52.00 0.00 59.00 HIPS 24.50 20.50 16.5012.50 But-TPP 6.00 6.00 7.00 7.00 LLDPE 1.00 1.00 1.00 1.00 AO 626 0.300.30 0.30 0.30 ZnS 0.10 0.10 0.10 0.10 MgO 0.10 0.10 0.10 0.10 Glassfiber 20.00 20.00 20.00 20.00 PROPERTIES UL 94 rating at 1.5 mm V-1 V-0V-1 V-0 HDT at 3.2 mm (° C.) 132 132 135 137

Examples 22 and 23, Comparative Examples 29 and 30

These inventive and comparative examples, all with 30% glass fiberreinforcement, further illustrate that the improved flame retardancyassociated with the use of poly(phenylene ether)-polysiloxane blockcopolymer reaction product rather than poly(phenylene ether) homopolymercan be obtained without substantially sacrificing heat resistance.Comparative Example 30 also illustrates that a reduction of HIPSconcentration and increases in flame retardant and poly(phenylene ether)homopolymer, all relative to Comparative Example 29, are not sufficientto result in V-0 flame performance at 1.5 millimeters.

TABLE 8 C. Ex. 29 Ex. 22 C. Ex. 30 Ex. 23 COMPOSITIONS PPE 0.46 49.000.00 51.50 0.00 PPE-Si 0.00 53.00 0.00 56.00 HIPS 12.00 8.00 8.50 4.00But-TPP 7.50 7.50 8.50 8.50 LLDPE 1.00 1.00 1.00 1.00 AO 168 0.30 0.300.30 0.30 ZnS 0.10 0.10 0.10 0.10 MgO 0.10 0.10 0.10 0.10 Glass fiber30.00 30.00 30.00 30.00 PROPERTIES UL 94 rating at 1.5 mm V-1 V-0 V-1V-0 HDT at 3.2 mm (° C.) 136 135 135 136

Examples 24-26, Comparative Examples 31-36

These inventive and comparative examples demonstrate that it is alsopossible to achieve a UL 94 rating of V-0 at a thickness of 0.75millimeters in a 20% glass fiber reinforced composition containingpoly(phenylene ether)-polysiloxane block copolymer, while maintaining aheat deflection temperature greater than 110° C. Comparative Example 36achieved a V-0 rating but was deficient in heat deflection temperature.

TABLE 9 Ex. 24 Ex. 25 Ex. 26 C. Ex. 31 C. Ex. 32 COMPOSITIONS PPE-Si57.81 59.80 61.79 0.00 0.00 PPE 0.40 0.00 0.00 0.00 57.81 54.83 PPE 0.460.00 0.00 0.00 0.00 0.00 BPADP 19.90 17.91 15.92 19.90 22.89 Glass fiber19.90 19.90 19.90 19.90 19.90 LLDPE 1.49 1.49 1.49 1.49 1.49 AO 168 0.100.10 0.10 0.10 0.10 ZnS 0.15 0.15 0.15 0.15 0.15 MgO 0.15 0.15 0.15 0.150.15 Carbon black 0.50 0.50 0.50 0.50 0.50 PROPERTIES UL 94 rating atV-0 V-0 V-0 V-1 V-1 0.75 mm HDT (° C.) 113 121 128 119 109 Flex. modulus6094 6178 6104 6530 6570 (MPa) Flex. strength (MPa) 155 158 158 160 155C. Ex. 33 C. Ex. 34 C. Ex. 35 C. Ex. 36 COMPOSITIONS PPE-Si 0.00 0.000.00 0.00 PPE 0.40 51.84 0.00 0.00 0.00 PPE 0.46 0.00 57.81 54.83 51.84BPADP 25.87 19.90 22.89 25.87 Glass fiber 19.90 19.90 19.90 19.90 LLDPE1.49 1.49 1.49 1.49 AO 168 0.10 0.10 0.10 0.10 ZnS 0.15 0.15 0.15 0.15MgO 0.15 0.15 0.15 0.15 Carbon black 0.50 0.50 0.50 0.50 PROPERTIES UL94 rating at 0.75 mm V-1 V-1 V-1 V-0 HDT (° C.) 100 120 110 100 Flex.modulus (MPa) 6661 6638 6539 6717 Flex. strength (MPa) 145 161 153 146

Examples 27-43, Comparative Examples 37-39

These examples illustrate the attainment of a UL 94 V-0 rating at athickness of 1.5 millimeters by compositions comprising as little as 0.5weight percent of a poly(phenylene ether)-polysiloxane block copolymerreaction product. They further illustrate compositions comprising afirst poly(phenylene ether) (derived from the poly(phenyleneether)-polysiloxane block copolymer reaction product) and a secondpoly(phenylene ether) (separately added; see Examples 28-43).

Notched Izod values and unnotched Izod values, each expressed in unitsof joules/meter, were determined according to ASTM D256-08 at 25° C.using a hammer energy of 2 foot-pounds (2.71 joules), and barcross-sectional dimensions of 3.2 by 12.7 millimeters. Flexural modulus,flexural stress at yield, and flexural stress at break values, each inunits of megapascals, were determined at 23° C. according to ASTM D790-07e1 using 6.4 millimeter thick bars, a support span of 101.6millimeters, a test speed of 2.54 millimeters/minute (0.1 inch/minute;Procedure A), and three specimens per composition. Tensile modulus andtensile stress at break values, each expressed in units of megapascals,and tensile elongation at break values, expressed in units of percent,were determined according to ASTM D 638-08 at 23° C. using a Type I barhaving a thickness of 3.2 millimeters, a gage length of 50 millimeters,and a testing speed of 5 millimeters per minute.

The results demonstrate that compositions with 0.5 to 40 weight percentpoly(phenylene ether)-polysiloxane block copolymer reaction productexhibit a UL 94 V-0 rating at a thickness of 1.5 millimeters. Althoughphysical properties were not measured for all samples, the availableresults show that compositions with 2 to 40 weight percentpoly(phenylene ether)-polysiloxane block copolymer reaction productfurther exhibit a heat deflection temperature of at least 150° C.determined according to ASTM D 648-07 using a stress of 1.82 megapascals(MPa) and a sample thickness of 6.4 millimeters, and a flexural modulusof at least 5,000 megapascals measured at 23° C. according to ASTM D790-07e1 using a sample thickness of 6.4 millimeters. ComparativeExamples 37 and 38, without poly(phenylene ether)-polysiloxane blockcopolymer, and Comparative Example 39, with only 0.4 weight percentpoly(phenylene ether)-polysiloxane block copolymer, do not achieve a UL94 V-0 rating at a thickness of 1.5 millimeters.

TABLE 10 Ex. 27 Ex. 28 Ex. 29 Ex. 30 Ex. 31 COMPOSITIONS PPE-Si 68.240.0 30.0 20.0 10.0 PPE 0.33 0.0 0.0 0.0 0.0 0.0 PPE 0.30 0.0 30.8 39.348.8 56.8 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR4.0 0.0 0.0 0.0 0.0 SEBS 0.0 1.0 2.0 2.0 3.0 AO 626 0.8 0.0 0.0 0.0 0.0AO 168 0.0 0.2 0.2 0.2 0.2 BPADP 7.0 8.0 8.5 9.0 10.0 Glass fiber 20.020.0 20.0 20.0 20.0 Polysiloxane content 3.4 2.0 1.5 1.0 0.5 PROPERTIESUL Rating at 1.5 mm V-0 V-0 V-0 V-0 V-0 UL Rating at 1.0 mm V-0 V-0 V-0V-0 V-0 HDT (° C.) 153 159 159 157 153 Notched Izod (J/m) 69.8 87.8 95.290.8 96 Unnotched Izod (J/m) 338 466 478 492 457 Flex. modulus (MPa)5460 5240 5210 5090 5180 Flex. stress at yield (MPa) 131 140 143 140 143Flex. stress at break (MPa) 132 141 140 140 143 Tens. modulus (MPa) 69006818 6784 6768 6784 Tensile stress at break (MPa) 114 119 118 120 120Tens. elong. at break (%) 2.2 2.5 2.5 2.5 2.5 C. Ex. 37 Ex. 32 Ex. 33Ex. 34 Ex. 35 COMPOSITIONS PPE-Si 0.0 20.0 10.0 8.0 6.0 PPE 0.33 0.0 0.00.0 0.0 0.0 PPE 0.30 65.8 47.8 57.8 59.8 61.8 PDMS/silica 0.0 0.0 0.00.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS 4.0 2.02.0 2.0 2.0 AO 626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.20 0.20BPADP 10.0 10.0 10.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0Polysiloxane content 0.0 1.0 0.5 0.4 0.3 PROPERTIES UL Rating at 1.5 mmV-1 V-0 V-0 V-0 V-0 UL Rating at 1.0 mm V-1 — — — — HDT (° C.) 153 153154 155 155 Notched Izod (J/m) 101 79.8 82.0 86.6 83.3 Unnotched Izod(J/m) 515 495 516 503 511 Flex. modulus (MPa) 5270 5330 5390 5400 5400Flex. stress at yield (MPa) 147 — — — — Flex. stress at break (MPa) 144133 135 134 138 Tens. modulus (MPa) 6694 — — — — Tensile stress at break(MPa) 117 — — — — Tens. elong. at break (%) 2.5 — — — — Ex. 36 Ex. 37 C.Ex. 38 Ex. 38 Ex. 39 COMPOSITIONS PPE-Si 4.0 2.0 0.0 4.0 2.0 PPE 0.330.0 0.0 0.0 63.8 65.8 PPE 0.30 63.8 65.8 67.8 0.0 0.0 PDMS/silica 0.00.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS2.0 2.0 2.0 2.0 2.0 AO 626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.200.20 BPADP 10.0 10.0 10.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0Polysiloxane content 0.2 0.1 0.0 0.2 0.1 PROPERTIES UL Rating at 1.5 mmV-0 V-0 V-1 V-0 V-0 UL Rating at 1.0 mm — — — — — HDT (° C.) 155 155 156— — Notched Izod (J/m) 81.1 79.5 81.3 — — Unnotched Izod (J/m) 496 475475 — — Flex. modulus (MPa) 5460 5490 5560 — — Flex. stress at yield(MPa) — — — — — Flex. stress at break (MPa) 133 138 135 — — Tens.modulus (MPa) — — — — — Tensile stress at break (MPa) — — — — — Tens.elong. at break (%) — — — — — Ex. 40 Ex. 41 Ex. 42 Ex. 43 C. Ex. 39COMPOSITIONS PPE-Si 1.0 0.50 1.60 0.80 0.40 PPE 0.33 66.8 67.3 66.2 67.067.4 PPE 0.30 0.0 0.0 0.0 0.0 0.0 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS 2.0 2.0 2.0 2.0 2.0 AO626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.20 0.20 BPADP 10.0 10.010.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0 Polysiloxane content0.05 0.025 0.08 0.04 0.02 PROPERTIES UL Rating at 1.5 mm V-0 V-0 V-0 V-0V-1 UL Rating at 1.0 mm — — — — — HDT (° C.) — — — — — Notched Izod(J/m) — — — — — Unnotched Izod (J/m) — — — — — Flex. modulus (MPa) — — —— — Flex. stress at yield (MPa) — — — — — Flex. stress at break (MPa) —— — — — Tens. modulus (MPa) — — — — — Tensile stress at break (MPa) — —— — — Tens. elong. at break (%) — — — — —

Example 44

This example illustrates a composition exhibiting high flame retardancy,heat resistance, and melt flow.

TABLE 11 Ex. 44 COMPOSITION PPE-Si 5.97 PPE 0.33 65.46 SEBS 1.99 AO 1680.20 BPADP 10.95 Carbon black 0.50 Glass fiber 14.93 Polysiloxanecontent 0.30 PROPERTIES UL Rating at 1.5 mm V-0 HDT (° C.) 152 Flex.modulus (MPa) 4790 Flex. strength (MPa) 132 MVR (cc/10 min) 24

1-2. (canceled)
 3. The article of claim 13, wherein the poly(phenyleneether)-polysiloxane block copolymer comprises a poly(phenylene ether)block comprising phenylene ether repeat units having the structure

and a polysiloxane block having the structure

wherein n is 30 to
 60. 4. The article of claim 13, wherein thepoly(phenylene ether)-polysiloxane block copolymer comprises apoly(phenylene ether)-polysiloxane multiblock copolymer.
 5. (canceled)6. The article of claim 13, wherein the reinforcing filler is selectedfrom the group consisting of glass fibers, carbon fibers, wollastonite,halloysite, clays, talcs, micas, glass flakes, solid glass beads, hollowglass beads, solid ceramic beads, hollow ceramic beads, and combinationsthereof.
 7. The article of claim 13, wherein the reinforcing fillercomprises glass fibers.
 8. The article of claim 13, wherein the flameretardant comprises the organophosphate ester.
 9. The article of claim8, wherein the organophosphate ester comprises bisphenol A bis(diphenylphosphate).
 10. The article of claim 13, wherein the flame retardantcomprises the phosphazene.
 11. The article of claim 10, wherein theflame retardant comprises a cyclic oligo(bis(phenoxy)phosphazene), alinear oligo(bis(phenoxy)phosphazene), a linearpoly(bis(phenoxy)phosphazene), a crosslinkedpoly(bis(phenoxy)phosphazene), or a combination thereof.
 12. The articleof claim 13, wherein the composition further comprises 1 to 10 weightpercent of an impact modifier selected from the group consisting ofrubber-modified polystyrenes, unhydrogenated block copolymers of analkenyl aromatic monomer and a conjugated diene, hydrogenated blockcopolymers of an alkenyl aromatic monomer and a conjugated diene,acrylate core-shell impact modifiers, and combinations thereof.
 13. Anarticle comprising a composition, wherein the article is a fuser holder;and wherein the composition comprises 2 to 10 weight percent of apoly(phenylene ether)-polysiloxane block copolymer reaction productcomprising a poly(phenylene ether)-polysiloxane block copolymer and afirst poly(phenylene ether); 55 to 75 weight percent of a secondpoly(phenylene ether); 5 to 25 weight percent of a flame retardantcomprising an organophosphate ester, a phosphazene, or a combinationthereof; and 10 to 35 weight percent of a reinforcing filler; whereinall weight percent values are based on the total weight of thecomposition.
 14. The article of claim 13, wherein the compositioncomprises 10 to 20 weight percent of the reinforcing filler, and thereinforcing filler comprises glass fibers.
 15. The article of claim 13,wherein the composition further comprises 1 to 5 weight percent of ahydrogenated block copolymer of an alkenyl aromatic compound and aconjugated diene.
 16. An article comprising a composition, wherein thearticle is a fuser holder; wherein the composition comprises 2 to 10weight percent of a poly(phenylene ether)-polysiloxane block copolymerreaction product comprising a poly(phenylene ether)-polysiloxane blockcopolymer and a first poly(phenylene ether); wherein the poly(phenyleneether)-polysiloxane block copolymer comprises a poly(phenylene ether)block comprising phenylene ether repeat units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; and wherein the first poly(phenylene ether)comprises poly(2,6-dimethyl-1,4-phenylene ether); 55 to 75 weightpercent of a second poly(phenylene ether) comprisingpoly(2,6-dimethyl-1,4-phenylene ether); 10 to 20 weight percent of areinforcing filler comprising glass fibers; 5 to 15 weight percent of aflame retardant comprising bisphenol A bis(diphenyl phosphate); and 1 to5 weight percent of a polystyrene-poly(ethylene-butylene)-polystyreneblock copolymer; wherein all weight percent values are based on thetotal weight of the composition. 17-20. (canceled)
 21. An articlecomprising a composition, wherein the article is selected from the groupconsisting of fan blades, battery parts for hybrid and electricvehicles, parts for automotive kinetic energy recovery systems, andelectric vehicle junction boxes; wherein the composition comprises 53 to63 weight percent of a poly(phenylene ether)-polysiloxane blockcopolymer reaction product comprising a poly(phenyleneether)-polysiloxane block copolymer and a first poly(phenylene ether);wherein the poly(phenylene ether)-polysiloxane block copolymer comprisesa poly(phenylene ether) block comprising phenylene ether repeat unitshaving the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; 15 to 25 weight percent of a reinforcing fillercomprising glass fibers; 15 to 25 weight percent of a flame retardantcomprising bisphenol A bis(diphenyl phosphate); and 0.5 to 3 weightpercent of a linear low density polyethylene; wherein all weight percentvalues are based on the total weight of the composition.